Abstract:Corrosion is a common form of durability degradation of steel bridges. Corrosion morphology affects stress distribution under cyclic loads and causes strain concentrations in pits, thus affecting the mechanical properties of steel structures, including ultra-low cycle fatigue (ULCF). To precisely simulate corrosion morphology and investigate the ULCF failure mechanism of corroded steel piers, a sculpting method was applied to mesh units using three-dimensional surface morphology data of corroded steel specimens. Moreover, the ULCF crack-initiation life was numerically predicted using the finite element model based on the cyclic void growth model (CVGM). The cumulative equivalent plastic strain, cyclic void growth index, and critical void growth index of corroded steel piers with different corroded morphologies were compared. Results reveal that, regardless of whether the pier is corroded, fatigue cracks tend to initiate at the weld toe at corners when exposed to cyclic loads under an oblique direction at the pier top. Additionally, the ULCF crack-initiation life in a corroded pier is less than that in an uncorroded pier, and it is significantly affected by a reduction in the pier wall thickness. Corrosion pits affect the position of ULCF crack initiation in a steel pier and cracks tend to initiate at the bottom of pits with large depth-to-diameter ratios. In the case of minor corrosion, the corrosion morphology affects the seismic performance of piers to a small extent.

Effect of structural damage on fatigue strength of aircraft skin structures

Effect Of Corroded Surface Morphology On Ultra-Low Cycle Fatigue Of Steel Bridge Piers

A Model for Ultra Low Cycle Fatigue Damage Prediction of Structural Steel

Ultra-low Cycle Fatigue Properties and Fracture Mechanism of Corroded Structural Steel

A Proposal on Ultra-Low Cycle Fatigue Damage Evaluation of Structural Steels

A New Approach for Studying Fatigue Damage

Improved Ultra-Low Cycle Fatigue Fracture Models for Structural Steels Considering the Dependence of Cyclic Damage Degradation Parameters on Stress Triaxiality

THE INFLUENCES OF CORROSION DAMAGE ON THE FATIGUE CRACK DEVELOPMENT OF CONCRETE STRUCTURES

Depth-sensing Indentation Measurement and Finite Element Analysis of Residual Stress Field Near Fatigue Crack Tip

Fatigue-driven failure criterion for progressive damage modelling and fatigue life prediction of composite structures

Surface Stress Analysis of Internally Corroded Pipes under External Pressure

Life Prediction of Corrosion-Fatigue Based on a New Crack Growth Rate Model with Damage and the Extended Finite Element Method

Correlation between the Geometric Parameters of Corrosion Pit and Stress Concentration Factor

Simulation Investigation on Environment-Induced Pitting Corrosion on the Metal Surface

Effects of Stress Ratios on Aero High-strength LD2CZ Aluminum Alloy Fatigue Crack Growth with Corrosion Damage

Structural mechanics model for anisotropic damage and fatigue life prediction method of face-centered cubic metal materials

Corrosion effects on the fatigue performance of high-strength bolted friction connections

Impact of alternating corrosion and fatigue on the fatigue life of a 7475-T7351 aluminum alloy in an aircraft beam structure

Damage-Accumulation-Induced Crack Propagation and Fatigue Life Analysis of a Porous LY12 Aluminum Alloy Plate

A simulation approach for corrosion-fatigue behaviour of metallic structures considering coupling effect

Detail Stress Analysis and Fatigue Crack Initiation Life Prediction of Riveted Joint