Abstract:A nanoporous composite film combined of conducting inorganic template (TiO2/SnO2) and conducting polymer catalyst (poly(3,4-ethylenedioxythiophene):polystyrenesulfonate, PEDOT:PSS) was developed as an alternative counter electrode for dye-sensitized solar cell (DSSC) through low temperature process. The TiO2/SnO2 template was first fabricated by coating a homogeneous TiO2 nanoparticles. blended paste containing a SnCl4 aqueous solution on the conductive substrate, followed by annealing at 150 degrees C. The counter electrode was then completed by spin coating the PEDOT:PSS aqueous solution into the template and drying at 80 degrees C. The obtained TiO2/SnO2/PEDOT:PSS (TSP) composite film exhibits more excellent catalytic activity for the triiodide reduction than the pristine PEDOT:PSS film, resulting in the significant improvements in the fill factor and efficiency of the cells. The values of the fill factor and efficiency respectively increase from 0.564 and 4.79% to 0.699 and 6.54%. Noted that the photovoltaic performances of the TSP based DSSC is very similar to those of the Pt based one. The fill factor and efficiency of the later are 0.696 and 6.48%, respectively. The outstanding properties of the TSP composite film used as the counter electrode can be ascribed to its prominent synergistic effects. In the TSP composite film, the conducting TiO2 is applied as the main skeleton material with the in-situ formed SnO2 as a binder to construct a nanoporous structure for the PEDOT:PSS coating and also to provide numerous high-speed conductive paths for the electron transportation from the substrate to the PEDOT:PSS coating, and the PEDOT:PSS adhered on the TiO2/SnO2 skeleton mainly acts as the catalyst to enlarge its surface area allowing for more active sites for the tri-iodide reduction.

Plastic Dye-Sensitized Solar Cells with Enhanced Performance Prepared from A Printable Tio2 Paste

Functions of Self-Assembled Ultrafine TiO2 Nanocrystals for High Efficient Dye-Sensitized Solar Cells

Improved Performance of Dye Sensitized Solar Cells Using Cu-doped TiO2 As Photoanode Materials: Band Edge Movement Study by Spectroelectrochemistry

Facile fabrication of highly porous photoanode at low temperature for all-plastic dye-sensitized solar cells with quasi-solid state electrolyte

Selective Laser Sintering Of Tio2 Nanoparticle Film On Plastic Conductive Substrate For Highly Efficient Flexible Dye-Sensitized Solar Cell Application

Effects of TiO2 paste components on properties of dye-sensitized solar cells

A Simple and Efficient Method Using Polymer Dispersion to Prepare Controllable Nanoporous TiO2 Anodes for Dye-Sensitized Solar Cells

Organic-free Anatase TiO2 Paste for Efficient Plastic Dye-Sensitized Solar Cells and Low Temperature Processed Perovskite Solar Cells

Nanostructured Mesoporous Titanium Dioxide Thin Film Prepared by Sol-Gel Method for Dye-Sensitized Solar Cell

Fabrication of Mesoporous TiO2 Electrodes by Chemical Technique for Dye-Sensitized Solar Cells

Solar-To-Electric Performance Enhancement by Titanium Oxide Nanoparticles Coated with Porous Yttrium Oxide for Dye-Sensitized Solar Cells

Photovoltaic Performance Improvement of Dye-Sensitized Solar Cells Through Introducing In-doped TiO2 Film at Conducting Glass and Mesoporous TiO2 Interface As an Efficient Compact Layer

Synthesis of dispersed long single-crystalline TiO 2 paste and its application in DSSC as a scattering layer

Enhanced Efficiency of Dye-Sensitized Solar Cell by High Surface Area Anatase-TiO 2 -Modified P25 Paste

Low Temperature Transfer of Well-Tailored TiO2 Nanotube Array Membrane for Efficient Plastic Dye-Sensitized Solar Cells

Nanoporous TiO2/SnO2/Poly(3,4-ethylene-dioxythiophene): Polystyrenesulfonate Composites As Efficient Counter Electrode for Dye-Sensitized Solar Cells

The effect of dispersion of TiO 2 nanoparticles on preparation of flexible dye-sensitized photoanodes

Preparation of Platinized Electrode Via Photo-Platinization Technique for Flexible Dye- Sensitized Solar Cells

Chemical Sintering by Chlorinated Carbon Compounds for Flexible Photoanodes of Dye-Sensitized Photovoltaic Cells

Indirect Preparation of Titanium Dioxide Oxidation Plating Layer as Photoelectrode Used in Dye-Sensitized Solar Cells

Dye-sensitized solar cells, from cell to module