Strain Rate Dependence of Stretch-Induced Crystallization and Crystal Transition of Poly(dimethylsiloxane)
Jingyun Zhao,Shengyao Feng,Wenwen Zhang,Wei Chen,Junfang Sheng,Wancheng Yu,Liangbin Li
DOI: https://doi.org/10.1021/acs.macromol.1c01407
IF: 5.5
2021-01-01
Macromolecules
Abstract:The stretch-induced crystallization (SIC) and crystal transition (SCT) of silica-reinforced poly(dimethylsiloxane) (PDMS) in parameter spaces of strain rate (from 0.002 to 2 s(-1)) and temperature (from ca. -35 to -75 degrees C) have been studied via in situ synchrotron radiation wide-angle X-ray scattering. Non-equilibrium SIC/SCT diagrams in the strain rate-temperature space have been established. The effects of the strain rate on the SIC/SCT are mainly manifested on the following two aspects. First, stretching of PDMS at different strain rates can induce the formation of four different crystal forms beta', beta, alpha', and alpha. The specific crystal form during the SIC has shown to be determined by the competition between the kinetic and thermodynamic factors. A higher strain rate and temperature are favorable for the formation of kinetically stable crystal forms alpha' and alpha. While at low strain rates and temperatures, the thermodynamically stable forms beta' and beta are preferred. Second, among the four crystal forms, the alpha' form appears over a wide range of strain rates and temperatures because of its strong adaptability to the stretching field. For the alpha' crystal formed during the SIC, the strain rate can regulate the crystallite size, the tilt degree of chains in the crystal, and also the spatial distributions of crystals and network strands. We have found that the critical stress to trigger the SCT of alpha'-alpha and the state of network strands at the onset of the SCT are closely associated with the microstructural features of crystals and network strands formed in the preceding SIC. Three simplified mechanical models have been proposed to clarify the SCT mechanisms of alpha'-alpha at the low, moderate, and high strain rates.