High-Temperature-Resistant Polymer Gel System With Metal-Organic Mixed Cross-Linking Agents
xiaoyun zhang,sisi zhang,liang li,ruonan wu,dongming liu,jihui wu,wei wu
DOI: https://doi.org/10.1002/app.42261
IF: 3
2015-01-01
Journal of Applied Polymer Science
Abstract:A high-temperature (200 degrees C)-resistant polymer gel system was developed from partially hydrolyzed polyacrylamide (HPAM), chromium lactate (CrL), and water-soluble phenol/formaldehyde resin (WPF) mixed cross-linkers. Rheological measurements indicated that the gelation process of the gel system could be divided into four successive steps: induction, first cross-linking with metal cross-linker, secondary cross-linking with organic cross-linker, and stabilization. Effects of various parameters that affect the gelation time and gel strength including polymer concentration, cross-linker concentration, salinity, pH, and the gelation temperature were evaluated. Gelant formulated with 0.5 wt % HPAM, 0.1 wt % CrL, and 0.9 wt % WPF and treated at 80 degrees C for 48 h showed sufficient gelation time, high rigidity, and good thermal stability. Morphology observation by scanning electron microscopy (SEM) and atomic force microscopy (AFM) revealed that the gel had compact network microstructure. A cross-linking mechanism for the gel system was proposed based on the gelation process and experimental results. (c) 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015, 132, 42261.