Enhancement of Modulus, Strength, and Toughness in Poly(methyl methacrylate)-Based Composites by the Incorporation of Poly(methyl methacrylate)-Functionalized Nanotubes
David Blond,Valerie Barron,Manuel Ruether,Kevin P. Ryan,Valeria Nicolosi,Werner J. Blau,Jonathan N. Coleman
DOI: https://doi.org/10.1002/adfm.200500855
IF: 19
2006-01-01
Advanced Functional Materials
Abstract:Poly(methyl methacrylate) (PMMA)-functionalized multiwalled carbon nanotubes are prepared by in situ polymerization. Infrared absorbance studies reveal covalent bonding between polymer strands and the nanotubes. These treated nanotubes are blended with pure PMMA in solution before drop-casting to form composite films. Increases in Young's modulus, breaking strength, ultimate tensile strength, and toughness of x1.9, x4.7, x4.6, and x13.7, respectively, are observed on the addition of less than 0.5 wt % of nanotubes. Effective reinforcement is only observed up to a nanotube content of approximately 0.1 vol %. Above this volume fraction, all mechanical parameters tend to fall off, probably due to nanotube aggregation. In addition, scanning electron microscopy (SEM) studies of composite fracture surfaces show a polymer layer coating the nanotubes after film breakage. The fact that the polymer and not the interface fails suggests that functionalization results in an extremely high polymer/nanotube interfacial shear strength.