Structure and Dielectric Temperature Characteristic of High Temperature BZSPTx Piezoelectric Ceramics with Low Sc Content

SHI Wei,ZHU Ya,XIAO Dingquan,ZHU Jianguo

DOI: https://doi.org/10.7521/j.issn.0454-5648.2013.04.01

2013-01-01

Abstract:In order to reduce the cost of the high Curie temperature TC BiScO3–PbTiO3piezoelectric ceramics,(1–x)(0.15BiScO3– 0.85PbTiO3)–xBi(Zn1/2Ti1/2)O3(BZSPTx,x is mole fraction) ceramics were prepared via conventional solid reaction.The microstructure phase and dielectric temperature character of BZSPTx ceramics were characterized by X-ray diffraction,scanning electron microscopy and dielectric temperature characterization method,respectively.The results show that the perovskite phase with the single tetragonal peroviskite structure in the Bi(Zn1/2Ti1/2)O3content(x) range from 0.075 to 0.125 of the ceramics can be obtained.Furthermore,the BZSPTx ceramics had a greater lattice distortion(c/a 1.1),a lower piezoelectricity and a high TC 520 ℃.It was also indicated that the ceramics with the greatest value of the piezoelectric constant(d33= 76 pC/N) at x = 0.075 and high TC of 536 ℃ could be promising candidate materials for the high temperature operating environment.