Three-Dimensional Hierarchical MoSe 2 /N, F Co-Doped Carbon Heterostructure Assembled by Ultrathin Nanosheets for Advanced Lithium-Ion Batteries
Qinqin Liang,Lixuan Zhang,Man Zhang,Qichang Pan,Yu Li,Chunlei Tan,Fenghua Zheng,Youguo Huang,Hongqiang Wang,Qingyu Li
DOI: https://doi.org/10.1021/acssuschemeng.0c04719
2020-08-28
Abstract:MoSe<sub>2</sub> has attracted great interest as an anode material for lithium-ion batteries (LIBs) thanks to its high capacity. Nevertheless, the poor cycle performance caused by the huge volume change during the lithiation/delithiation process seriously limits its practical application in LIBs. Herein, a 3D hierarchical MoSe<sub>2</sub>/N, F co-doped carbon (MoSe<sub>2</sub>/NFC) heterostructure is prepared via a simple method. Notably, the N, F co-doped heterostructure can expand the (002) plane of MoSe<sub>2</sub>, which contributes in facilitating Li<sup>+</sup> insertion/extraction. Furthermore, N, F co-doped carbon confined MoSe<sub>2</sub> nanosheets to form a 3D hierarchical heterostructure, leading to fast electron/ion transfer, buffering of the volume change, and prevention of the aggregation of MoSe<sub>2</sub> nanosheets during the repeated discharge/charge process. Therefore, the MoSe<sub>2</sub>/NFC composite exhibits good rate performance and ultra-long cycling life when applied in LIBs. A high capacity of 452.9 mAh g<sup>–1</sup> is maintained at 5 A g<sup>–1</sup>, and a high capacity of 598.3 mAh g<sup>–1</sup> is obtained after 1000 cycles at 2 A g<sup>–1</sup>.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c04719?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c04719</a>.TGA curves of MoSe<sub>2</sub>/C and MoSe<sub>2</sub>/NFC; N<sub>2</sub> adsorption isotherms and pore size distribution of the MoSe<sub>2</sub>/NFC composite; SEM and TEM images of MoSe<sub>2</sub> and MoSe<sub>2</sub>/C composites; charge/discharge curves of MoSe<sub>2</sub> and MoSe<sub>2</sub>/C composites; comparison of our work with previous MoSe<sub>2</sub>-based materials (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c04719/suppl_file/sc0c04719_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology