Abstract:Zn-Cu-codoped SnO2 nanoparticles have been synthesized by chemical precipitation method. All nanoparticles are crystalline, with the average size increases from 2.55 nm to 4.13 nm as the calcination temperature increases from 400 degrees C to 600 degrees C. The high calcination temperature can enhance the crystalline quality and grain growth. The oxygen content decreases with decreasing calcination temperature; at a low temperature of 400 degrees C, Zn-Cu-codoped SnO2 nanoparticles are in a rather oxygen-poor state having many oxygen vacancies. The optical band gap energies of Zn-Cu-codoped SnO2 nanoparticles calcined at 400 degrees C and 600 degrees C are decreased from 3.93 eV to 3.62 eV due to quantum confinement effects. Both samples exhibit room-temperature ferromagnetism, with a larger saturation magnetization at 400 degrees C due to the presence of large density of defects such as oxygen vacancies. Zn-Cu-codoped SnO2 nanoparticles exhibit large optical band gap energies and room temperature ferromagnetism, which make them potential candidates for applications in optoelectronics and spintronics.

Synthesis And Characterization Of Multicomponent Cu-2(Fexzn1-X)Sns4 Nanocrystals With Tunable Band Gap And Structure

Solution-based Synthesis and Characterization of Cu2FeSnS4 Nanocrystals

Zn-Cu-codoped SnO2 Nanoparticles: Structural, Optical, and Ferromagnetic Behaviors

ChemInform Abstract: Crystal Phase‐Controlled Synthesis of Cu2FeSnS4 Nanocrystals with a Band Gap of Around 1.5 Ev.

Crystal phase-controlled synthesis of Cu 2FeSnS 4 nanocrystals with a band gap of around 1.5 eV

A Facile and Low-Cost Synthesis of Cu2ZnSn(SxSe1−x)4 Nanocrystals with Tunable Composition and Optical Band Gap

Composition- and Band-Gap-Tunable Synthesis of Wurtzite-Derived Cu2ZnSn(S1–xSex)4 Nanocrystals: Theoretical and Experimental Insights

A general synthesis of Cu-In-S based multicomponent solid-solution nanocrystals with tunable band gap, size, and structure

Alloyed (Znse)(x)(cuinse2)(1-X) and CuInSe(x)S(2-x) Nanocrystals with a Monophase Zinc Blende Structure over the Entire Composition Range.

Studies of synthesis and optical properties of ZnS nanocrystals

Synthesis, Characterization, and Properties of Nanocrystalline Cu2sns3

Wurtzite CuIn(S x Se 1- x ) 2 Nanocrystals: Colloidal Synthesis and Band-Gap Engineering

Linearly arranged polytypic CZTSSe nanocrystals

Alloyed Semiconductor Nanocrystals with Broad Tunable Band Gaps

ChemInform Abstract: Alloyed Semiconductor Nanocrystals with Broad Tunable Band Gaps.

Hydrothermal Synthesis and Photoluminescence Properties of La2−xEuxSn2O7 (x=0–2.0) Nanocrystals

Tunable crystal structure of Cu–Zn–Sn–S nanocrystals for improving photocatalytic hydrogen evolution enabled by copper element regulation

Facile hydrothermal synthesis of hydrotropic Cu2ZnSnS 4 nanocrystal quantum dots: Band-gap engineering and phonon confinement effect

Controllable Transformation from Rhombohedral Cu1.8S Nanocrystals to Hexagonal CuS Clusters: Phase- and Composition-Dependent Plasmonic Properties

Synthesis and Optical Properties of Zns : Cu(Ii) Nanoparticles

Facile synthesis and characterization of CuInS2 nanocrystals with different structures and shapes