Color Point Tuning by Partial Ba2+ Substitution of Ca2+ in (ca1−xbax)3(po4)2 Phosphor for White Light Emitting Diodes

Yinqun Li,Hua Yu,Degang Deng,Youjie Hua,Shilong Zhao,Guohua Jia,Huanping Wang,Lihui Huang,Yinyan Li,Chenxia Li,Shiqing Xu

DOI: https://doi.org/10.1016/j.jssc.2012.12.012

IF: 3.3

2012-01-01

Journal of Solid State Chemistry

Abstract:A potential phosphor (Ca1−xBax)3(PO4)2:Eu2+ was synthesized by a solid-state reaction. X-ray diffraction (XRD) analysis confirmed the formation of (Ca1−xBax)3(PO4)2 crystal phase. With the Ba2+ content increasing, the bandgap of (Ca1−xBax)3(PO4)2 increases from 5.5 to 5.9eV, and the crystal field splitting between the two lowest Eu2+ 5d levels is enhanced from 6085 to 6808cm−1 in (Ca1−xBax)3(PO4)2. As a result, the emission peak of (Ca1−xBax)3(PO4)2: Eu2+ shifts from 447 to 550nm, which means that the emission color alters from blue to yellow. The redshift of the emission band of (Ca1−xBax)3(PO4)2:Eu2+ was explained based on crystal field strength, covalence, Stokes shift. The results revealed that partial substitution of Ca2+ by Ba2+ ions was therefore a much considerable way to shift the color point of LEDs.