Abstract:This paper presents an experimental study on simultaneously measuring the elastic modulus and residual stress of a thermal barrier coating (TBC) after different isothermal heat treatments. The elastic modulus and residual stress of TBCs were theoretically analyzed based on composite beam bending theory. Thereafter, an experimental setup was established combining the 3D digital image correlation method with the bending test to obtain the curvature changes in the TBC sample. Finally, the elastic modulus and residual stress of the ceramic layer with different isothermal heat treatments were obtained. The results show that the elastic modulus of the ceramic layer measured under compression is greater than that under tension, and the elastic modulus of the ceramic layer increases first and then tends to be stable as the heat treatment time increases. In addition, the residual stress of the TBCs ceramic layer quickly changes from compressive stress to tensile stress with heat treatment, and the tensile stress increases with the increase in thermal exposure time. Furthermore, the reasons for the change tendency were analyzed according to the variation in porosity and microstructures by processing the scanning electron microscope (SEM) figures. The results demonstrate that simultaneously determining the elastic modulus and residual stress of TBC based on combining the 3D digital image correlation method with the bending test is effective and reliable.

Thermal deformation of Y2O3 partially stabilized ZrO2 coatings by digital image correlation method

Thermal Conductivity Imaging of Thermal Barrier Coatings

Characterization of the Strain in the Thermal Barrier Coatings Caused by Molten CaO-MgO-Al2O3-SiO2 Using a Digital Image Correlation Technique

Analysis of thermal shock performance of Y2O3 stabilized ZrO2 (YSZ) coating based on residual stress and micro-morphology

Research of Nd2O3 and Yb2O3 Co-doped YSZ Thermal Barrier Coatings Produced by Electron Beam Physical Vapor Deposition

A real time deformation evaluation method for surface and interface of thermal barrier coatings during 1100°C thermal shock

Investigation of the Microstructures and Thermal Barrier Properties of YSZ Thermal Barrier Coatings

Development of Deposition Beam Current Dependent Microstructure and Nanomechanical Properties in ZrO2-8wt%Y2O3 Thermal Barrier Coatings Produced by Electron Beam-Physical Vapor Deposition Technique

Microstructure and thermo-physical properties of yttria stabilized zirconia coatings with CMAS deposits

Study of microstructure, electronic structure and thermal properties of Al2O3-doped tetragonal YSZ coatings

Measurement of the Elastic Modulus and Residual Stress of Thermal Barrier Coatings Using a Digital Image Correlation Technique

Preparation, Thermophysical Properties, and Thermal Shock Resistance of Yb2O3-doped YSZ Coatings

Impedance Spectroscopy Study of High-Temperature Oxidation of Gd2O3-Yb2O3 Codoped Zirconia Thermal Barrier Coatings

Evolution of residual stress in air plasma sprayed yttria stabilised zirconia thermal barrier coatings after isothermal treatment

Preparation and High-Temperature Performance of Sc2O3-Y2O3 Co-Stabilized ZrO2 Thermal Barrier Coatings

Thermal Cycling Behavior and Failure Mechanism of Yb2O3-doped Yttria-Stabilized Zirconia Thermal Barrier Coatings

High-Temperature Digital Image Correlation Method for Full-Field Deformation Measurement at 1200 Degrees C

Modeling the Cracking Process of the YSZ Thermal Barrier Coating under the Thermal Shocking Loads

Effect of Isothermal Heat Treatment on Plasma‐Sprayed Yttria‐Stabilized Zirconia Studied by Impedance Spectroscopy

An Accurate and Rapid Method to Compare Thermal Insulation Capacity of Nine Gd-Yb-YSZ Coatings

Microstructure, Thermal Conductivity and Thermal Cycling Behavior of Thermal Barrier Coatings Prepared by Plasma Spray Physical Vapor Deposition