Reaction Route Optimized LiBH 4 for High Reversible Capacity Hydrogen Storage by Tunable Surface-Modified AlN
Jiuyi Zhu,Yuchen Mao,Hui Wang,Jiangwen Liu,Liuzhang Ouyang,Min Zhu
DOI: https://doi.org/10.1021/acsaem.0c02140
IF: 6.4
2020-11-13
ACS Applied Energy Materials
Abstract:LiBH<sub>4</sub> (lithium borohydride) is a promising high capacity hydrogen storage material but suffering from its high dehydrogenation temperature and poor reversibility. To solve this problem, surface-modified AlN (aluminum nitride) was prepared by the alcoholysis process of LiBH<sub>4</sub> and composited with LiBH<sub>4</sub>. By controlling the temperature of the drying process, it can tune the sorts and quantities of the functional groups on AlN. The de/rehydrogenation of LiBH<sub>4</sub> is greatly improved by compositing it with surface-modified AlN because oxygen atoms in functional groups promote the decomposition of intermediates of LiBH<sub>4</sub> and H<sup>δ+</sup> (positive hydrogen atom) reacting with H<sup>δ−</sup> (negative hydrogen atom) in LiBH<sub>4</sub>. Besides, AlN provides the pathway of H and Li atoms to improve the kinetics of the de/rehydrogenation of LiBH<sub>4</sub>. Freeze-dried AlN containing O–H and C–H groups shows the best catalytic effect on the hydrogen storage reaction of LiBH<sub>4</sub>. The optimized composite could release a stable capacity of more than 6.1 wt % after cycling, which has potential applications in high-temperature environment hydrogen storage.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.0c02140?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.0c02140</a>.XPS spectra N1s and Al2p of AlN, XPS spectra of AlN, dehydrogenation of LiBH<sub>4</sub> + AlN(freeze) at room temperature, SEM and EDS images of LiBH<sub>4</sub> + AlN(@60C) after the third cycle, XRD patterns of ball-milled and first dehydrogenated LiBH<sub>4</sub> + AlN(freeze) composites, FT-IR spectra of ball-milled LiBH<sub>4</sub> + AlN(freeze) composites, hydrogen storage properties of ball-milled pure LiBH<sub>4</sub>, TPD-MS and isolated dehydrogenation curves of LiBH<sub>4</sub> + AlN(@60C) composites, first and second dehydrogenation curves of LiBH<sub>4</sub> + AlN(@60C), optimizing the mass ratio of LiBH<sub>4</sub> + AlN(@60C) composite, and the hydrogen content of AlN(freeze) by an envelope calculation (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.0c02140/suppl_file/ae0c02140_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels