Preparation and characterization of a novel washcoat material and supported Pd catalysts

Xiang-Xiang Li,Min Chen,Xiao-Ming Zheng

DOI: https://doi.org/10.1134/S0023158413050108

2013-01-01

Kinetics and Catalysis

Abstract:A nanosized Ce 0.5 Mn 0.5 O 1.5 powder was successfully synthesized by macromolecule surfactant modified method and then it was used as the cordierite honeycomb washcoat of VOCs combustion catalysts. The effect of Ce-Mn-O powder with different Ce/Mn molar ratio on the catalytic activity and the cohesive ability of washcoat on the cordierite honeycomb substrate was also investigated. The structure and catalytic properties of Ce 0.5 Mn 0.5 O 1.5 washcoat were characterized by X-ray powder diffraction (XRD), transmission electron microscopy (TEM), atomic force microscopy (AFM), differential thermal analysis and thermo-gravimetric analysis (TG/DTA), and N 2 adsorption and desorption techniques. The results indicated that the Ce 0.5 Mn 0.5 O 1.5 powder belongs to a novel washcoat with the advantages of strong cohesiveness, high surface area and without agglomeration even after 1000°C calcination. The total oxidation temperature for toluene, acetone and ethyl acetate over the 0.1 wt % Pd/Ce 0.5 Mn 0.5 O 1.5 /cordierite honeycomb catalysts was at 200, 220 and 220°C, respectively. Compaired with the catalysts without Ce 0.5 Mn 0.5 O 1.5 washcoat, the catalyst with Ce 0.5 Mn 0.5 O 1.5 as washcoat on the cordierite honeycomb could improve the dispersion of PdO and shows a good catalytic activity for toluene, acetone and ethyl acetate.