Abstract:We present a facile and effective one-pot strategy to synthesize nanoporous copper (NPC) with controlled hierarchical pore size distributions which can be fabricated through chemical dealloying of the melt-spun Al-35Cu alloy in a 10wt.% sodium hydroxide (NaOH) solution at an elevated temperature. These NPC ribbons are composed of large-sized ligament–pore structures (several hundred nanometers) at outer layers coupled with small-sized those (several ten nanometers) at inner layers. Both large- and small-sized pores are 3D, open and bicontinuous. The formation of the novel NPC ribbons can be well explained based upon the synergetic action between diffusion mechanism and pore size effect. According to the ligament sizes, the surface diffusivities at inner and outer layers of Cu adatoms can be evaluated as 3.80×10−20, 1.63×10−18, 3.54×10−18, 6.83×10−18 and 7.88×10−20, 5.41×10−17, 4.36×10−16, 4.27×10−15m2s−1 for the dealloying at 298, 333, 348 and 363K, respectively. The activation energies and diffusion constants at inner and outer layers are also measured as 47.7kJmol−1, 1.41×10−17m2s−1 and 145.3kJmol−1, 4.21×10−14m2s−1, suggesting the existence of a complicated dealloying mechanism. Additionally, the length scales of ligaments/pores at inner and outer layers can be modulated by simply changing the dealloying temperature or duration at a fixed elevated temperature.

Hierarchical Porous Copper Materials: Fabrication and Characterisation

Fabrication and Compression Properties of Bulk Hierarchical Nanoporous Copper with Fine Ligament

Fabrication and characterization of bulk nanoporous Cu with hierarchical pore structure

Dealloying Solution Dependence of Fabrication, Microstructure and Porosity of Hierarchical Structured Nanoporous Copper Ribbons

Hierarchical Porous Cu with Trimodal Porosity Produced Through Investment Casting and Dealloying

Formation and characterization of Monolithic nanoporous copper by chemical dealloying of Al-Cu alloys

A Facile One-Pot Route to Fabricate Nanoporous Copper with Controlled Hierarchical Pore Size Distributions Through Chemical Dealloying of Al–Cu Alloy in an Alkaline Solution

Structure Evolution of Nanoporous Copper by Dealloying of Al 17-33 At% Cu Alloy

Microstructures and mechanical properties of bulk nanoporous copper fabricated by dealloying Al-Cu alloys

Formation of Nanoporous Copper Through Dealloying of Dual-Phase Cu-Mn-Al Alloy: the Evolution of Microstructure and Composition

Directional Hierarchical Porous Cu Prepared by One-Step Etching 3D Printed Fe-Cu Alloy with Two-Stage Phase Separation Structure

Nanoporous Copper Fabricated by Dealloying Mn–Cu Precursors with Minor Nickel Element Addition and Heat Treatment Coarsening

Fabrication of A Hierarchical Trimodal Structure with Nano-Cellular Cu2o, Nano-Porous Cu and Micro-Porous Gasar Cu

A Novel Approach to Fabricate Hierarchical Porous Metals with Both Improved Capillarity and Permeation Performance

Microstructure evolution of monolithic nanoporous copper from dual-phase Al 35 atom % Cu alloy

Preparation and Characterization of Nanoporous Cu6Sn5/Cu Composite by Chemical Dealloying of Al–Cu–Sn Ternary Alloy

A Study of Electroplated Nanoporous Copper Using Aberration-Corrected Transmission Electron Microscopy

Synthesis and mechanical properties of porous metals with inverted dealloying structure

Preparation of nanoporous copper foil by chemical dealloying from electro-deposited CuZn alloy

Hierarchical nested-network porous copper fabricated by one-step dealloying for glucose sensing

Fabrication of bulk nanoporous copper by dealloying of Cu0.3Mn0.7 alloy