Abstract:A novel carbonaceous SiC/mullite composite aerogel is derived from catechol-formaldehyde/silica/alumina hybrid aerogel (CF/SiO2/AlOOH) via polymer-derived ceramics route (PDCR). The effects of the reactants concentrations on the physicochemical properties of the carbonaceous SiO2/Al2O3 aerogel and SiC/mullite aerogel are investigated. The mechanism of the textural and structural evolution for the novel carbonaceous SiC/mullite is further discussed based on the experimental results. Smaller reactants concentration is favorable to formation of mullite. Reactants concentration of 25% is selected as the optimal condition in considering of the mullite formation and bulk densities of the preceramic aerogels. Spherical large silica particles are also produced during heat treatment, and amorphous silica is remained after this reaction. With further heat treatment at 1400°C, silicon carbide and mullite coexist in the aerogel matrix. The mullite addition decreases the temperature of SiC formation, when compared with the conventional methods. However, after heat treatment at 1450°C, the amount of mullite begins to decrease due to the further reaction between carbon and mullite, forming more silicon carbide and alumina. The carbonaceous SiC/mullite can be transferred to SiC/mullite binary aerogel after carbon combustion under air atmosphere. The carbonaceous SiC/mullite has a composition of SiC (31%), mullite (19.1%), SiO2 (14.4%), and carbon (35%). It also possesses a 6.531nm average pore diameter, high surface area (69.61m2/g), and BJH desorption pore volume (0.1744cm3/g). The oxidation resistance of the carbonaceous SiC/mullite is improved for 85°C when compared with the carbon based aerogel.

Synthesis and characterization of carbon nanofibers doped silica aerogels

Fabrication of SiCN(O) Aerogel Composites with Low Thermal Conductivity by Wrapping Mesoporous Aerogel Structures over Mullite Fibers

Synthesis and characterization of ambient-dried microglass fibers/silica aerogel nanocomposites with low thermal conductivity

Flexible and Compressible Nanostructure-Assembled Aramid Nanofiber/Silica Composites Aerogel

Cellulose Nanofibril (CNF) Based Aerogels Prepared by a Facile Process and the Investigation of Thermal Insulation Performance

Silica-Bacterial Cellulose Composite Aerogel Fibers with Excellent Mechanical Properties from Sodium Silicate Precursor

Multiscale Assembly of Superinsulating Silica Aerogels Within Silylated Nanocellulosic Scaffolds: Improved Mechanical Properties Promoted by Nanoscale Chemical Compatibilization

Robust Carbonaceous Nanofiber Aerogels from All Biomass Precursors

Silk Nanofibers/Carbon Nanotube Conductive Aerogel

Self-reinforcement of Light, Temperature-Resistant Silica Nanofibrous Aerogels with Tunable Mechanical Properties

Cellulose-Silica Composite Aerogels Prepared with Sodium Silicate by Freeze Drying Method

Multiscale Nanocelluloses Hybrid Aerogels for Thermal Insulation: the Study on Mechanical and Thermal Properties.

Comparative Study of Aerogels Obtained from Differently Prepared Nanocellulose Fibers.

SiO2 aerogel multiscale reinforced by glass fibers and SiC nanowhiskers for thermal insulation

Nanofibrous Aerogel Bulk Assembled by Crosslinked SiC/SiOx Core-Shell Nanofibers with Multifunctionality and Temperature-Invariant Hyperelasticity.

In-situ synthesis and textural evolution of the novel carbonaceous SiC/mullite aerogel via polymer-derived ceramics route

Robust Silica–Agarose Composite Aerogels with Interpenetrating Network Structure by in Situ Sol–Gel Process

Self-catalyzed Gelling Synthesis of Aerogels with Inorganic and Organic Nanocomponents for Thermal Insulation and CO 2 Capture

Enhancing the thermal insulation properties of polymer-derived SiCN(O) ceramic aerogels with a polysilazane-precursor design

Synthesis and Textural Evolution of Mesoporous Si3N4 Aerogel with High Specific Surface Area and Excellent Thermal Insulation Property Via the Urea Assisted Sol-Gel Technique

Preparation of the Novel B4C–SiC Composite Aerogel with High Compressive Strength and Low Thermal Conductivity