Study on the evolution of phase and properties for ternary La-Y-Ni-based hydrogen storage alloys with different stoichiometric ratios
Xiangyang He,Wei Xiong,Li Wang,Baoquan Li,Jin Li,Shujuan Zhou,Jiaxuan Li,Huizhong Yan
DOI: https://doi.org/10.1016/j.jallcom.2022.166064
IF: 6.2
2022-07-10
Journal of Alloys and Compounds
Abstract:In recent years, some progress has been made in the development and application of the highly anticipated La-Y-Ni hydrogen storage alloy system. However, the relationship between the structure and properties of materials has not been studied systematically and thoroughly. In this paper, the evolution law of AB 3 -, A 2 B 7 - and A 5 B 19 -type phases for La-Y-Ni-based hydrogen storage alloys was proposed. The single-phase LaY 2 Ni 9 (AB 3 ), La 2 Y 4 Ni 21 (A 2 B 7 ) and La 5 Y 10 Ni 57 (A 5 B 19 ) alloys were synthesized by powder sintering method at 1173, 1353 and 1423 K, respectively. The XRD and SEM results of the alloys show that LaY 2 Ni 9 alloy has a single PuNi 3 phase (3 R), La 2 Y 4 Ni 21 alloy is composed of Ce 2 Ni 7 phase (2 H) and Gd 2 CO 7 phase (3 R), and La 5 Y 10 Ni 57 alloy contains Pr 5 Co 19 phase (2 H) and Ce 5 Co 19 phase (3 R). Among the three alloys, the La 2 Y 4 Ni 21 alloy has the largest hydrogen storage capacity (1.59 wt%) in solid /H 2 reaction at 313 K. The target alloys all exhibit excellent electrochemical activation ability. The maximum discharge capacity of LaY 2 Ni 9 , La 2 Y 4 Ni 21 and La 5 Y 10 Ni 57 alloys decreases gradually, but their cycle stability increases in turn. The high-rate discharge performance of La 2 Y 4 Ni 21 alloy is the best, because its exchange current density ( I 0 = 75.55 mA/g) and hydrogen diffusion coefficient ( D 0 = 2.51 ×10 −10 cm 2 /s) cooperate well. It is hoped that these findings can offer theoretical guidance and technical assistance for the development of La-Y-Ni-based hydrogen storage alloys.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering