Abstract:A red-emitting phosphor Ca 2.91 Si 2 O 7 :0.09Eu 3+ with partial Al 3+ /P 5+ substitution on Si 4+ was synthesized via a simple solid-state method, and the effects of the introduction of the M 3+/5+ (M = Al, P) ions on the crystal structure and photoluminescence performance of Ca 2.91 Si 2− x M x O 7 :0.09Eu 3+ phosphors were investigated. The X-ray diffraction (XRD), energy-dispersive X-ray spectroscopy (EDS), and X-ray photoelectron spectroscopy (XPS) results revealed that the structure of Ca 3 Si 2 O 7 remained the same after the introduction of Al 3+ and P 5+ ions. The characteristic emission of Eu 3+ -doped Ca 3 Si 2− x M x O 7 phosphors exhibited two main peaks at 617 nm (red) and 593 nm (orange) under excitation at 394 nm, which originated from the 5 D 0 → 7 F 2 and 5 D 0 → 7 F 1 electron transitions of Eu 3+ ions. After the partial substitution of Al 3+ and P 5+ , the red emission intensities of the Ca 2.91 Si 2 O 7 :0.09Eu 3+ phosphors were significantly enhanced by 1.88- and 1.42-fold, respectively, which is attributed to the crystal-field effect around Eu 3+ . Meanwhile, the luminescence intensities of the Ca 2.91 Si 1.96 Al 0.04 O 7 :0.09Eu 3+ and Ca 2.91 Si 1.94 P 0.06 O 7 :0.09Eu 3+ phosphors at 210 °C were 79.36% and 77.53% of those at 30 °C, respectively, indicating their excellent thermal stability. Moreover, the as-prepared Ca 2.91 Si 1.96 Al 0.04 O 7 :0.09Eu 3+ and Ca 2.91 Si 1.94 P 0.06 O 7 :0.09Eu 3+ red-emitting phosphors were combined with a near-ultraviolet chip of 395 nm to fabricate red-light-emitting diode (LED) and white (w)-LED devices with excellent chromaticity features. In summary, Al 3+ /P 5+ -substituted Ca 2.91 Si 2 O 7 :0.09Eu 3+ can serve as red-emitting phosphors for applications in w-LEDs.

Tunable Orange Red Phosphors: S2−-doped High Temperature Phase Ca3SiO4Cl2:Eu2+ for Solid-State Lighting

Ca(La1-xEux)4Si3O13 red emitting phosphor for white light emitting diodes

Red-emitting Oxonitridosilicate Phosphors Sr2SiNzO4−1.5z:Eu2+ for White Light-Emitting Diodes: Structure and Luminescence Properties

The pure-phase Ba3−xCaxSi6O12N2:Eu2+ green phosphor: synthesis, photoluminescence and thermal properties

Synthesis, Crystal Structure, and Luminescence Properties of Tunable Red-Emitting Nitride Solid Solutions (Ca1-Xsrx)(16)si17n34:Eu2+ for White Leds

Luminescence Properties of Ca2si5n8:Eu2+ Prepared by Gas-Pressed Sintering Using Baf2 As Flux and Cation Substitution

Europium-Doped Calcium Silicate Nanoparticles as High-Quantum-Yield Red-Emitting Phosphors

A single host phosphor Ca3(SiO3)3:Eu2+, Mn2+ with good monodispersity for phosphor-converted white LEDs

Photoluminescence Evolution and High Thermal Stability of Orange Red-Emitting Ba3-xSrxZnNb2O9: Eu3+ Phosphors

Synthesis and tunable emission from yellow-green to red-orange of Ca3MgSi2O8:Eu3+, Dy3+ phosphor

Dual-strategy of Eu2+ sensitization and Ca2+ substitution improves the luminescence properties of phosphor Sr2La8(SiO4)6O2:Eu

Structural, Compositional and Photoluminescence Studies of Li4SrCa(SiO4)2: Eu3+ Red Phosphor Synthesized by Solid State Reaction Method

A Giant Stokes Shift in Wide‐Band Red Phosphor [Ca0.33(Sr1‐xBax)0.67]7(SiO3)6Cl2: Eu2+

Red/Blue-Shift Dual-Directional Regulation Of Alpha '(L)-(Ca, Sr)(2)Sio4:Eu2+ Phosphors Resulting From The Incorporation Content Of Eu2+/Sr2+ Ions

Enhanced red luminescence of Ca3Si2−xMxO7:Eu3+ (M = Al, P) phosphors via partial substitution of Si4+ for applications in white light-emitting diodes

Eu3+-doped Bi4Si3O12 red phosphor for solid state lighting: microwave synthesis, characterization, photoluminescence properties and thermal quenching mechanisms

Photoluminescence properties of novel blue-light excited orange-red phosphors Sr3Al2Si3O12:Eu2+

Tunable photoluminescence and energy transfer of novel phosphor Sr9La2W4O24:Sm3+, Eu3+ for near-UV white LEDs

Synthesis and characterization of highly Eu3+-doped CaY2Sb2(ZnO4)3 red phosphors with abnormal thermal quenching performance for w-LEDs application

Blue-To-Orange Tunable Luminescence From Europium Doped Yttrium-Silicon-Oxide-Nitride Phosphors

Intense Red Light Emission Of Eu3+-Doped Sr3b2sio8 For White Light-Emitting Diodes