Abstract:A series of BaLi 2− x Na x Ti 6 O 14 (0≤ x ≤2) compounds as lithium storage materials were synthesized by a facile solid-state method. X-ray diffraction Rietveld refinement shows that the Bragg positions correspond to the BaLi 2 Ti 6 O 14 , indicating a successful preparation. The Na + ions doped BaLi 2 -Ti 6 O 14 compounds have larger unit-cell volume than the pristine one because ionic radius of Na + ion is 55% larger than that of Li + ion. SEM shows that the BaLi 2− x Na x Ti 6 O 14 ( x =0, 0.5 and 1) powders show similar irregular shaped particles between 500 and 1000 nm. However, BaLi 2− x Na x Ti 6 O 14 ( x =1.5 and 2) powders show similar rod-like shape. CV reveals that the passivating film is mainly formed during the first insertion process, and the solid electrolyte interface film on the surface of BaLi 2− x Na x Ti 6 O 14 (0≤ x ≤2) is formed below 0.7 V in the first cycle. Compared with other samples, BaLi 0.5 Na 1.5 Ti 6 O 14 exhibits higher reversible capacity, better rate capability and superior cyclability. BaLi 0.5 Na 1.5 Ti 6 O 14 delivers the delithiation capacities of 162.1 mA h g −1 at 50 mA g −1 , 158.1 mA h g −1 at 100 mA g −1 , 156.7 mA h g −1 at 150 mA g −1 , 152.2 mA h g −1 at 200 mA g −1 , 147.3 mA h g −1 at 250 mA g −1 and 142 mA h g −1 at 300 mA g −1 , respectively. An interesting thing is that BaNa 2 Ti 6 O 14 as anode also shows an acceptable electrochemical performance. All these improved electrochemical performances of BaLi 0.5 Na 1.5 Ti 6 O 14 are attributed to the lowest polarization and the highest lithium ion diffusion coefficient among all samples. Hence, BaLi 0.5 Na 1.5 Ti 6 O 14 with excellent cycling performance, simple synthesis route and wide discharge voltage range can be a possible anode candidate for lithium-ion batteries.

Temperature-dependent Lithium Storage Behavior in Tetragonal Boron (B50) Thin Film Anode for Li-ion Batteries

A Lithium Metal Anode Surviving Battery Cycling above 200 °C.

Electrochemical Mechanism of Amorphous Boron Oxide Thin Film with Lithium

All Boron-Based 2D Material As Anode Material in Li-ion Batteries

In situ formed three-dimensional (3D) lithium–boron (Li–B) alloy as a potential anode for next-generation lithium batteries

Performance Improvement Strategies of Boron-Doped Lithium-Rich Layered Oxide Cathode Materials for Wide Temperature Condition

Lithium barium titanate: A stable lithium storage material for lithium-ion batteries

Ultrathin and High-Modulus LiBO2 Layer Highly Elevates the Interfacial Dynamics and Stability of Lithium Anode under Wide Temperature Range

A Wide Temperature 10 V Solid-state Electrolyte with a Critical Current Density of over 20 mA cm-2

Boron Embedded In Metal Iron Matrix As A Novel Anode Material Of Excellent Performance

High-Performance Borophene/Graphene Heterostructure Anode of Lithium-Ion Batteries Achieved Via Controlled Interlayer Spacing

Structure and Electrochemical Performance of BaLi2−x Na X Ti6O14 (0≤x≤2) As Anode Materials for Lithium-Ion Battery

Triphenyl Borate as an Effective Film-Modification Additive for Regulating the Solid Electrolyte Interphase Formed on Graphite and Silicon Based Anode

Enhanced Electrochemical Performance of the Li 2 B 12 H 12 -Li 2 B 10 H 10 -LiBH 4 Electrolyte

Superior Wide-Temperature Lithium Storage in a Porous Cobalt Vanadate

A Thermally Conductive Separator for Stable Li Metal Anodes.

Observation of High-Capacity Monoclinic B-Nb2O5 with Ultrafast Lithium Storage

Theoretical investigation of Ti2B monolayer as powerful anode material for Li/Na batteries with high storage capacity

The Effect of Boron Doping on Structure and Electrochemical Performance of Lithium-Rich Layered Oxide Materials.

Ternary Lithium Nickel Boride with 1D Rapid‐Ion‐Diffusion Channels as an Anode for Use in Lithium‐Ion Batteries

Boron-Doped Spherical Hollow-Porous Silicon Local Lattice Expansion toward a High-Performance Lithium-Ion-Battery Anode.