The Effect of Boron Doping on Structure and Electrochemical Performance of Lithium-Rich Layered Oxide Materials.

Jiatu Liu,Shuangbao Wang,Zhengping Ding,Ruiqi Zhou,Qingbing Xia,Jinfang Zhang,Libao Chen,Weifeng Wei,Peng Wang
DOI: https://doi.org/10.1021/acsami.6b03056
IF: 9.5
2016-01-01
ACS Applied Materials & Interfaces
Abstract:Polyanion doping shows great potential to improve electrochemical performance of Li-rich layered oxide (LLO) materials. Here, by optimizing the doping content and annealing temperature, we obtained boron-doped LLO materials Li1.2Mn0.54Ni0.13Co0.13BxO2 (x = 0.04 and 0.06) with comprehensively improved performance (94% capacity retention after 100 cycles at 60 mA/g current density and a rate capability much higher compared to that of the pristine sample) at annealing temperatures of 750 and 650 °C, respectively, which are much lower than the traditional annealing temperature of similar material systems without boron. The scenario of the complex crystallization process was captured using Cs-corrected high-angle annular dark field scanning transmission electron microscopic (HAADF-STEM) imaging techniques. The existence of layered, NiO-type, and spinel-like structures in a single particle induced by boron doping and optimization of annealing temperature is believed to contribute to the remarkable improvement of cycling stability and rate capability.
What problem does this paper attempt to address?