Abstract:Single crystals of SrAl2O4 prepared with 0.2–2.0 mol% Eu2O3 were synthesized using the optical floating zone method using ceramic rods that had been prepared under reducing conditions to favor conversion of Eu3+ to Eu2+. Samples were then characterized by a combination of X-ray diffraction (XRD), X-ray photoelectron (XPS), positron annihilation, electron paramagnetic resonance (EPR), photoluminescence excitation (PLE) and photoluminescence (PL) spectroscopic techniques, and their excited state lifetimes were measured. XRD showed that the crystal samples were all in the monoclinic phase. EPR and PL techniques indicated that they contained Eu2+, although XPS indicated that the Eu3+ reduction was only ∼50%. Positron annihilation spectroscopy demonstrated that all of the samples contained a considerable number of defects that act as positron traps, and were influenced by the amount of Eu2O3 used in the crystal synthesis. These defects did not show an EPR signal, which suggests that they may correspond structural vacancies, possibly due to the presence of cation vacancies as a result of incorporation of some Eu3+ in the divalent cation sites. However, EPR did reveal a small amount of anionic paramagnetic defects, and showed a progressive broadening of the Eu2+ resonance for crystals synthesized with Eu2O3 concentrations >0.5 mol%. The intensity of the PLE spectra increased with Eu2O3 concentration, and the relative proportions of the peaks at 3.62 eV (360 nm) and 3.13 eV (417 nm) changed with Eu2O3 concentration. The PL spectra showed a broad green emission peak at 2.52 eV (518 nm), which is attributed to 4f65d-4f7 charge transfer transitions in Eu2+. Both its intensity and fluorescence decay time increased with Eu2O3 concentration, reached a maximum with the sample prepared with 1.5 mol% Eu2O3, then decreased with higher Eu2O3 concentrations.

Influence of doping concentration on valence states of europium in SrAl2O4:Eu phosphors

Luminescence of Eu2+ in Sr2Al6O11 based phosphor

Synthesis, structure, and luminescence properties of SrSiAl<sub>2</sub>O<sub>3</sub>N<sub>2</sub>:Eu<sup>2+</sup> phosphors for light-emitting devices and field emission displays

Investigations On Valence-Change Behaviors Of Europium Ions In Eu-Doped Aluminate And Silicate Phosphors

Effects of synthesis temperature and Eu2O3 concentration on the crystalline phases and photoluminescence properties of SrAl2O4 phosphors

Luminescence and microstructural characteristics of Eu2O3-doped SrAl2O4 single crystals

Eu 3+ -doped Sr 2 (Al 1−x Mg x )(Al 1−x Si 1+x )O 7 phosphors: electronic, crystal structures and photoluminescence properties

Preparation and Luminescent Properties of SrAl2O4:Eu2+, Dy3+ Phosphor Via a Flux-Coprecipitation Method

Rare-earth Ion (Eu3+ and Dy3+) substituted SrAl2O4 phosphor: A study of structural and luminescence properties

Influence of Mn2+ doping on the emission spectrum of Sr2La8(SiO4)6O2:Eu(2+,3+) phosphor

Preparation and properties of Eu2+doped strontium phosphate blue phosphor by Sol-gel method

Effect of Y3+ Ions Doping on the Luminescence Properties of Sr1-xCaxSi2O2N2:Eu2+ Phosphors

The Eu2+-concentration Dependence of Photoluminescence Behaviors in Β-Sialon:Eu2+ Green Phosphors Prepared by Combustion Synthesis

Enhanced luminescence of Eu3+ in LaAl2B4O10 via energy transfer from Dy3+ doping

A Study on Thermal Quenching Mechanism in Sr2Si5N8 :Eu Red Phosphors with Different Eu Concentration

Structural and Luminescent Properties of Solid-Solution Phosphor BaxSr1-xAl2O4: Eu2+

Effect of Comburent Ratios on Combustion Synthesis of Eu-doped Β-Sialon Green Phosphors

Photo- and mechano-luminescent properties of color-tunable (Eu2+, Dy3+)-co-doped strontium/calcium aluminate phosphor

Influence of different additives on the luminescent properties of Sr4Al14O25:Eu, dy phosphor materials

Luminescence properties and energy transfer study of color temperature tunable CaSrSiO4:Dy3+,Eu3+ white phosphors

Design and Characterization of Eu2+/Ln3+ Co-doped SrAl2Si2O8 Photostimulated Phosphors for Optical Information Storages