Abstract:It has been reported recently that some Eu 3+ doped nanocrystalline silicate and oxide were with higher quenching concentrations in comparison with the corresponding bulk materials. Computer simulation has shown that the size confinement and the existence of high density surface states affected significantly the quenching processes of the rare earth dopants in nanoparticles. To understand the feature of the energy transfer process in rare earth doped nanoparticles is important for further seeking applicable nano phosphors . This paper reported, the preparation of a series of Y 2O 2S∶Tb 3+ nanocrystals with uniform sizes and varied Tb 3+ concentrations. The mean size of all the samples prepared was evaluated, based on the X ray diffraction pattern, to be about 20nm. Emission spectra of Tb 3+ in nanocrystalline Y 2O 2S with different Tb 3+ concentrations were measured under 257nm excitation. With increasing Tb 3+ concentration, the luminescence intensity of both the 5D 4 → 7F J and 5D 3 → 7F J transitions increases at first and then decreases. Emission intensities reach their maximum at the Tb 3+ concentration of 0 6% for the 5D 3 emission and of 6 4% for the 5D 4 emission. The lifetime of the 5D 3 level is 0 31ms in the sample with 0 065% Tb concentration, comparably shorter than 0 78ms in bulk Y 2S 2O∶0 3%Tb. This fact indicates that the surface states do act as the quenching centers for the luminescence , and the increasing of quenching concentration comes probably from the lower quantum efficiency of the nanocrystals. The dependences of the intensity on Tb concentration and the decay curves of both 5D 3 and 5D 4 emissions fit with theory. The quenching of the 5D 3 state is governed by dipole dipole interaction, while that of the 5D 4 state by exchange interaction. Both the intensity and temporal analyses coincide and result in the same conclusion. Similar to bulk material, concentration quenching of the 5D 3 state is due to cross relaxation . The mechanism of the concentration quenching of the 5D 4 state is that the energy migrates among the Tb ions and is trapped finally by quenching centers, most likely, the surface states.

Concentration Quenching and Resultant Photoluminescence Adjustment for Ca3Si2O7:Tb3+ Green-Emitting Phosphor

Luminescence Properties And Energy Transfer Of Ce3+,Tb3+-Coactivated-Sialon Phosphors

Photoluminescence of Tb3+ Doped SiNx Films Grown by Plasma-Enhanced Chemical Vapor Deposition

Preparation and luminescence properties of Ce3+ and Tb 3+ co-doped glasses and glass ceramics containing SrF2 nanocrystals

Synthesis and luminescent characteristics of green-emitting (Sr 1− x M x ) 2 SiO 4 :Tb 3+ (M = Ba, Ca) phosphors

Study on Mechanism Controlling 5 D 3 / 5 D 4 Emissions of Tb 3+ in Glasses

Synthesis and Luminescence Properties of Ca3Y2Si3O12∶Tm3 + , Yb3 + Upconversion Phosphors

Photoluminescence of Tb3+-doped SiNx films with different Si concentrations

Cathodoluminescence Properties of Ba3Si6O9N4:Eu2+ Phosphors

Color point tuning for Ce3+ and Tb3+ activated Sr5(BO3)3F phosphors

Preparation of CaYAl3O7:Ce3+, Tb3+ Blue-Green Phosphors by Sol-Gel Process

Tunable Color Emissions upon UV Irradiation from Tb3+:Y2SiO5 Phosphor

Photoluminescence Properties and Energy Transfer in Color Tunable BaY2Si3O10:Ce,Tb Phosphors

Concentration Quenching of Tb3 + Emissions in Y2O2S Nanocrystals

Enhancing the Emission Intensity and Decreasing the Full Widths at Half Maximum of Ba3Si6O12N2:Eu(2+) by Mg(2+) Doping.

Tb 3+ and Sm 3+ co-doped Ca 2 La 3 (SiO 4 ) 3 F phosphor: synthesis, color regulation, and luminescence properties

Luminescence Enhancement of Ce3+/Tb3+ Co-Doped SiO2 Thin Film on Silicon Substrate Prepared by Sol-Gel Spin Coating Process

Photoluminescence evolutions and physical mechanism discussions of Sr1.95-(Ca/Ba) MgSi2O7:Eu2+ phosphors

Luminescent properties and energy transfer mechanism from Tb3+ to Eu3+ in color adjustable nano Ca5(PO4)3(OH): Eu3+,Tb3+ phosphors

Concentration-dependent tunable luminescence and highly thermal stability of Tb3+-activated KSrBP2O8 phosphor

Luminescence Property and Energy Transfer Behavior of Apatite-Type Ca4La6(SiO4)4(PO4)2O2:Tb3+, Eu3+ Phosphor