Tunable Color Emissions upon UV Irradiation from Tb3+:Y2SiO5 Phosphor

Vijay Singh,M. Seshadri,M. Radha,Chaitali M. Mehare,S. J. Dhoble,Ji Bong Joo

DOI: https://doi.org/10.1007/s11664-024-10985-2

IF: 2.1

2024-04-02

Journal of Electronic Materials

Abstract:A series of terbium-activated yttrium oxyorthosilicate (Tb 3+ :Y 2 SiO 5 ) phosphor was prepared through the sol–gel technique at a high calcination temperature of 1100°C. The phase purity was examined by the x-ray diffraction (XRD) analysis and found to be X1 type for all series of samples. The existence of functional groups in the prepared samples was confirmed by Fourier-transform infrared (FT-IR) spectroscopy. The sample exhibited absorption bands of Si-O-Si and Y-O groups at wavenumbers between 717 cm −1 and 550 cm −1 , and the NO 3 groups appeared between 800 cm −1 and 1020 cm −1 in the FT-IR spectra. Under 244-nm excitation, the photoluminescence spectra were recorded in the 350 to 650 nm wavelength range. A possible cross-relaxation mechanism between the 5 D 3 and the 5 D 4 levels for the concentration quenching of two distinct emission transitions has been described in detail. The dipole–dipole interaction is most responsible for concentration quenching, as evidenced by the Dexter theory. The CIE chromaticity analysis of the Y 2 SiO 5 :Tb 3+ phosphor was illustrated by a CIE 1931 color calculator. These findings demonstrate the suitability of the Tb 3+ -activated Y 2 SiO 5 matrix as a UV-excitable, color-tunable emitter with Tb 3+ ion variations and an efficient green light-emitting phosphor in the fields of solid-state lighting devices.

engineering, electrical & electronic,materials science, multidisciplinary,physics, applied