Rapid fluorescence assay for Sudan dyes using polyethyleneimine-coated copper nanoclusters
Yu Ling,Jia Xing Li,Fei Qu,Nian Bing Li,Hong Qun Luo
DOI: https://doi.org/10.1007/s00604-014-1214-9
2014-01-01
Mikrochimica Acta
Abstract:We report that the intensity of the blue fluorescence of copper nanoclusters coated with polyethyleneimine (PEI) is strongly reduced in the presence of the food dyestuffs Sudan I-IV. This finding was exploited in a label-free fluorescence assay for these Sudan dyes both in ethanol and aqueous solutions. The PEI-capped nanoclusters have an average diameter of 1.8 nm and are displaying, under 355 nm excitation, a blue emission at 480 nm that matches the absorption bands of the Sudan dyes. The clusters are stable in solution for at least 1 month. Under optimum conditions, this assay can be applied to the quantification of the dyes Sudan I, II, III, and IV, respectively, in the 0.1−30, 0.1–30, 0.1–25, and 0.1–25 μM concentration ranges, and the detection limits (3σ/slope) are 65, 70, 45, and 50 nM, respectively. The capability of reducing the fluorescence of the PEI-capped copper nanoclusters is directly related to the number of the functional groups in that Sudan III and IV give lower detection limits. This analytical scheme exhibits a remarkably high selectivity for the Sudan dyes over potentially interfering substances. The method was successfully applied to determine Sudan I, II, III, and IV in hot chilli powder. Figure The blue fluorescence emission of copper nanoclusters coated with polyethyleneimine (PEI) is strongly reduced in the presence of Sudan I-IV. This finding was exploited in a label-free fluorescence assay for these Sudan dyes both in ethanol and aqueous solutions.