Study on Growth and Properties of Tm~(3+)/Ho~(3+) Doped Gd_3Ga_5O_(12)～2.0 μm Infrared Laser Crystal
WANG Yan,TU Chao-yang,ZHOU Han,LI Jian-fu,YOU Zhen-yu,ZHU Zhao-jie
2011-01-01
Abstract:High quality Tm3+∶GGG,Yb3+/ Tm3+∶GGG,Cr3+/ Tm3+∶GGG,Tm3+/Ho3+∶GGG and Cr3+/Tm3+/Ho3+∶GGG crystals with the largest size 25 mm×(30-40) mm have been grown by Czochralski method.The absorption spectra,fluorescence spectra as well as fluorescence decay curves of all these crystals were measured at room temperature.The spectral properties were discussed,and Judd-Ofelt theory was used on some crystals to obtain intensity parameters and other important spectral parameters.The emission cross-sections,quantum efficiency of the transitions corresponding to ~2.0 μm wavelength were calculated.The results show that the codopant Yb3+ and Cr3+ made the absorption of Tm∶GGG crystal in the bands with peaks near 980 nm and near 451 nm,628 nm much stronger,which are suitable for pump by LD and Xenon lamp effectively.In the Tm3+ activated crystals,e.g.Tm3+∶GGG,Yb3+/Tm3+∶GGG,Cr3+/Tm3+∶GGG crystals,the strongest emission locates at ~2.0 μm;while in the Ho3+ activated crystals,e.g.Tm3+/Ho3+∶GGG,Cr3+/Tm3+/Ho3+∶GGG crystals,the strongest emission locates at ~2.08 μm.Laser characteristics of Cr3+/Tm3+/Ho3+∶Gd3Ga5O12 crystal with size 5 mm×45 mm were measured using the Xenon flash-lamp as the pumping source and 170 mW laser output was achieved within the range of 2.086-2.102 μm.