Abstract:In the present paper, to fabricate electroluminescent devices CdSe QDs were used as active materials, TPD (N,N'-biphenyl-N,N'-bis-(3-methylphenyl)-1,1'-biphenyl-4,4'-diamine) was used as a hole transport layer, and ZnS was used as an electron transport layer. The electroluminescent properties of the organic/inorganic composite ITO/TPD/CdSe QDs/ZnS/Ag light emitting devices were studied. Both TPD and CdSe QDs thin films were spin-coated and ZnS thin films were deposited by magnetron sputtering. The surfaces of the devices are smooth. The luminescence (EL) peak of the CdSe QDs is at 580 nm which is assigned to the band-edge exciton emission. Compared to the previous EL device of ITO/ZnS/CdSe QDs/ZnS/Ag, it is seen that the new devices do not display surface state related emission peaks and EL intensity is about 10 folds that of the previous device. The enhancement of luminescence efficiency is attributed to both of the excitation of CdSe QDs by accelerated electron collision and carriers injection into QDs: (1) electrons are accelerated by the ZnS layer and collide with CdSe QDs, which excites electrons in QDs to excited states and allows them to emit photons; (2) the holes injected into QDs recombine with some of electrons excited in the QDs. The authors further studied the influence of thickness variation of ZnS on the luminescent properties. ZnS thin films are of 80, 120, and 160 nm thickness, respectively. It was found that as the thickness of ZnS increases the threshold voltage rises and EL intensity increases, but breakdown voltage decreases. The EL peak position blue shifts when the thickness of ZnS decreases. The explanation of underlying mechanism is given.

Luminescence of Zno Films Covered by Ag: Influenceof Excitation Level and Ag Covering Method

Luminescence and Raman Scattering Properties of Ag-Doped Zno Films

Synthetic and Effect of Annealing on the Luminescent Properties of Zno Nanowire

Synthesis of Zno Nanoparticles with Controlled Shapes, Sizes, Aggregations, and Surface Complex Compounds for Tuning or Switching the Photoluminescence

Surface Morphology, Electrochemical and Electrical Performances of ZnO Thin Films Sensitized with Ag Nanoparticles by UV Irradiation

Effect of Solution Concentrations on Crystal Structure, Surface Topographies and Photoluminescence Properties of ZnO Thin Films

Photoluminescence And Extinction Enhancement From Zno Films Embedded With Ag Nanoparticles

Luminescence Properties of a Zn(ii) Supramolecular Framework: Easily Tunable Optical Properties by Variation of the Alkyl Substitution of (E)-N-(pyridine-2-ylethylidyne)arylamine Ligands

Enhancement of Zno Light Emission Via Coupling with Localized Surface Plasmon of Ag Island Film

Localized Surface Plasmon Enhanced Photoluminescence from Zno Films: Extraction Direction and Emitting Layer Thickness

Luminescence enhancement of Y2O3 thin films based on LSPR effect of Ag nanolayers

Photoluminescence and Resonant Raman Scattering in N-doped ZnO Thin Films

Electrophotoluminescence of Zno Film

[Influence of Parameters of ZnS Film on the Organic/inorganic Composite Luminescence Devices].

Excitation Wavelength Dependence Of The Visible Photoluminescence From Amorphous Zno Granular Films

Influence of Substrates in ZnO Devices on the Surface Plasmon Enhanced Light Emission

Luminescence Enhancement Due to Energy Transfer in ZnO Nanoparticles and Eu3+ Ions Co-Doped Silica

Enhanced Photocurrent and Photocatalytic Properties of Porous ZnO Thin Film by Ag Nanoparticles

Synthesis and luminescence properties of electrodeposited ZnO films

Scintillation and Luminescence Properties of the Zinc Oxide (zno) Doped Frit Crystal under Gamma Radiation

Photoluminescence of Zno and Mn-Doped Zno Polycrystalline Films Prepared by Plasma Enhanced Chemical Vapour Deposition