Effect of sintering condition and Ca2+-substitution on structural and electrical properties of lead-free Ba0.46Sr0.54TiO3 piezoceramics for uncooled IR detectors application
Dhanranjan Kumar,S. K. Rout,Kamana K. Mishra
DOI: https://doi.org/10.1007/s10854-024-12946-1
2024-06-21
Journal of Materials Science Materials in Electronics
Abstract:Barium titanate (BaTiO 3 ) is a potential material for producing¬†lead-free piezoceramics-based electronic devices. Microstructural engineering improves ceramic materials' dielectric, ferroelectric, and piezoelectric characteristics. This research aims to investigate the impacts of the sintering process and Ca 2+ substitution on microstructure and electromechanical performance of the Ba 0.46 Sr 0.54 TiO 3 (BST) and Ba 0.46 Sr 0.27 Ca 0.27 TiO 3 (BSCT) samples. The Ba 0.46 Sr 0.54 TiO 3 and Ba 0.46 Sr 0.27 Ca 0.27 TiO 3 powders were synthesized using a solid-state reaction technique. X-ray diffraction indicated the presence of tetragonal and cubic phases in a single-phase powder. The sintering condition influences grain size and density; as the sintering temperature rises, grain size reduces and density increases. We measured grain sizes in the range of 0.89¬†to 2.14¬†¬Ķm, and densities between 82% and 93.5% of the theoretical density, along with dielectric constants between‚ÄČ~‚ÄČ250 and‚ÄČ~‚ÄČ6000 at 5¬†kHz. A relation between grain sizes, dielectric constants, and polarization behaviors in response to temperature and electric field were all evaluated. The giant impact was observed in by the inclusion of Ca 2+ in recoverable energy densities and efficiency from 1.21¬†J/cm 3 (BST@1250¬†¬įC at 20¬†kV/cm) to 1.76¬†J/cm 3 (BSCT@1250¬†¬įC at 20¬†kV/cm) and 21.48 to 51.50¬†%, respectively, in prepared piezoceramics.
materials science, multidisciplinary,engineering, electrical & electronic,physics, applied, condensed matter