Abstract:Zr-17Nb alloy has been introduced as a candidate for spinal fixation rods because of its excellent mechanical properties and biocompatibility, low magnetic susceptibility, appropriate initial Young's modulus, remarkable deformation-induced variation of the Young's modulus, good ductility and relatively small springback. It has been recognized that nanotubular surface modification via anodic oxidation on metals is an efficient approach to highly improve biocompatibility of metallic implant. It is thus necessary to understand the formation of nanotubular arrays on Zr-17Nb alloy and carry out the evaluation on the nanotubular arrays. Electrochemical anodization was applied to modify the Zr-17Nb alloy surface to promote the bonding of alloy to human bone. Nanotubular arrays were formed on the surface of Zr-17Nb alloy by applying a 70 V constant potential in a glycerol electrolyte containing 0.35 mol/L NH4F and 5% H2O (volume fraction). XRD, SEM, HRTEM, EDS and XPS were used for the structural, morphological and compositional analyses of the nanotubular arrays. Results showed that during anodic oxidation process, the oxidation and dissolution rate of Zr were almost consistent with those of Nb. By extending the anodization duration from 10 min to 120 min, the diameter of nanotubes increased from about 20 nm to about 67 nm, and the length of nanotubes increased from about 2.4 mu m to about 6.8 mu m. After annealing at 450 degrees C for 60 min, the nanotube films were converted from amorphous to crystalline, mainly composed of orthogonal phase zirconia (ZrO2) and orthogonal phase zirconium niobium oxide (Nb2Zr6O17). The elastic modulus of the nanotube films decreased and the hardness increased. At the same time, the contact angle was reduced and the hydrophilicity was improved after annealing. Results demonstrate that highly ordered nanotubular arrays could be fabricate on the Zr-17Nb alloy. It is promising that nanotubular surface modification could be an efficient approach for enhancement of the biocompatibility of the alloy.

Surface modification of low-modulus Ti35NbXZr alloys with nanotube arrays

Effects of Zr Addition on the Deformation Behavior, Microstructure and Mechanical Properties of Dental Ti Alloys

Development and properties of dental Ti–Zr binary alloys

Fabrication and Properties of Anodic Oxide Nanotubular Arrays on Zr-17Nb Alloy

Biological Properties of Ti-Nb-Zr-O Nanostructures Grown on Ti35Nb5Zr Alloy

The Effect of Zr Content on the Microstructure, Mechanical Properties and Cell Attachment of Ti-35nb-Xzr Alloys

Construction of porous micro/nano structures on the surface of Ti–Mo–Zr alloys by anodic oxidation for biomedical application

Influence of Heterogeneous Microstructures on Anodization Behavior and Biocompatibility of Ti-15Zr Alloy

Antibacterial Ability of Zn Contained Nanotube Arrays on Titanium Surfaces

Ultra-high strength TiZrNbTa high entropy alloy substrate coated by coral-like metal oxide nanotubes to enhance biocompatibility

Wettability and in Vitro Bioactivity of Doped TiO2 Nanotubes

Cytocompatibility and osteogenic activity of Ta-Ti-O nanotubes anodically grown on Ti6Al4V alloy

Modified Surface Morphology of a Novel Ti–24Nb–4Zr–7.9Sn Titanium Alloy Via Anodic Oxidation for Enhanced Interfacial Biocompatibility and Osseointegration

Wettability and <I>In Vitro</I> Bioactivity of Doped TiO<SUB>2</SUB> Nanotubes: Wettability and <I>In Vitro</I> Bioactivity of Doped TiO<SUB>2</SUB> Nanotubes

Osteogenic Activity and Antibacterial Effects on Titanium Surfaces Modified with Zn-incorporated Nanotube Arrays

Compositional-segregation-induced dual-length-scale nanotubes for enhanced surface bioactivity of Ti-rich Ti65–Zr18–Nb16–Mo1 medium-entropy alloy

Anodic Fabrication and Bioactivity of Nb-Doped Tio2 Nanotubes

Fabrication of TiO2 nanotube array film on near-β titanium alloy and its effects on osteoblast growth

Novel Biocompatible Zr-Based Alloy With Low Young'S Modulus And Magnetic Susceptibility For Biomedical Implants

Novel Biocompatible Zr-Based Alloy with Low Young’s Modulus and Magnetic Susceptibility for Biomedical Implants

Mesoporous Surface Topography Promotes Bone Cell Differentiation on Low Elastic Modulus Ti–25Nb–25Zr Alloys for Bone Implant Applications