Abstract:The fabrication of a bionic super-hydrophobic metallic surface without any low-surface-energy modification is investigated, in which picosecond laser ablation, electropolishing and electrodeposition are used sequentially. The micro-cone structure is formed via laser ablation, and then the nano-pyramid structure is electrodeposited on the micro-cone structure, resulting in a hierarchical structure that is important for achieving super-hydrophobicity on an intrinsically hydrophilic material surface. In this study, the surface morphology and material removal mechanism are discussed with respect to the laser-ablated surface and the subsequent electropolished/electrodeposited surfaces. The condensation experiments results show that both types of surfaces are associated with relatively high contact angles (CAs) at normal temperatures, and the CAs are 147 degrees and 160 degrees, respectively. However, the CA on the laser-ablated surfaces at low temperatures decreases to as less as 107 degrees, which may be owing to the easy transition from Cassie state to a metastable state or even the Wenzel state, leading to a degraded hydrophobic surface. By contrast, the CA on the sequentially processed surfaces still maintains at 150 degrees, which should be attributed to the densely distributed nano-scale structures. The sequentially processed surfaces also show excellent long-term durability. Furthermore, this technique has been employed for fabricating super-hydrophobic surfaces with CM > 151 degrees and the sliding angles (SAs) < 8 degrees on the inclined surfaces with the inclination angle alpha < 30 degrees. Overall, the technique presented in this study supply a practical and reliable method for realizing the stable Cassie state and hence super-hydrophobicity on metallic surfaces.

Wettability Transition of Nickel Films with Micro-Nano Cones Array

Super-hydrophilicity to Super-Hydrophobicity Transition of a Surface with Ni Micro–nano Cones Array

Super-hydrophobic Nickel Films with Micro-Nano Hierarchical Structure Prepared by Electrodeposition

Fabrication of Modifier-Free Superhydrophobic Surfaces with Anti-Icing and Self-Cleaning Properties on Ti Substrate by Anodization Method

A facile process for preparing superhydrophobic nickel films with stearic acid

Superhydrophobic and anti-corrosion Cu microcones/Ni–W alloy coating fabricated by electrochemical approaches

Superhydrophobic Ni nanocone surface prepared by electrodeposition and its overall performance

Achieving of Bionic Super-Hydrophobicity by Electrodepositing Nano-Ni-pyramids on the Picosecond Laser-Ablated Micro-Cu-cone Surface

Superhydrophobic Nickel Films Fabricated by Electro/Electroless Deposition

Robust Ni/WC superhydrophobic surfaces by electrodeposition

A rapid one-step electrodeposition method for fabrication of the superhydrophobic nickel/cobalt alloy surfaces with excellent robustness and durability features

Preparation of super-hydrophobic Cu/Ni coating with micro-nano hierarchical structure

Wettability Transition on Micro-Nano Hierarchical Structured Ni20Cr Coating Surface by Selective Spontaneous Adsorption During Vacuum Evacuation

Wettability Evolution of Different Nanostructured Cobalt Films Based on Electrodeposition

Mechanism and Application of Nickel Nano-Cone by Electrodeposition on a Flexible Substrate

Tunable Wettability of Metallic Films with Assistance of Porous Anodic Aluminum Oxide

Applicable Superamphiphobic Ni/Cu Surface with High Liquid Repellency Enabled by the Electrochemical-Deposited Dual-Scale Structure.

Tunable wettability of jet electrodeposited micro-nano structures modified by laser radiation

Creating superhydrophobic surfaces with flowery structures on nickel substrates through a wet-chemical-process

Reversible Surface Wettability Transition Between Superhydrophobicity and Superhydrophilicity on Hierarchical Micro/Nanostructure Zno Mesh Films

Fabrication and Characterization of Superhydrophobic Surface by Electroplating Regular Rough Micro-Structures of Metal Nickel