Nanocrystal-constructed mesoporous single-crystalline Co3O 4 nanobelts with superior rate capability for advanced lithium-ion batteries

Hui Huang,Wenjun Zhu,Xinyong Tao,Yang Xia,Zhaoyang Yu,JunWu Fang,Yongping Gan,Wenkui Zhang

DOI: https://doi.org/10.1021/am301641y

2012-01-01

Abstract:In this paper, one-dimensional (1D) mesoporous single-crystalline Co 3O4 nanobelts are synthesized by a facile hydrothermal method followed by calcination treatment. The as-prepared nanobelts have unique mesoporous structures, which are constructed by many interconnected nanocrystals with sizes of about 20-30 nm. And typical size of the nanobelts is in the range of 100-300 nm in width and up to several micrometers in length. The BET surface area of Co3O4 nanobelts is determined to be about 36.5 m2 g-1 with dominant pore diameter of 29.2 nm. Because of the 1D structure, mesoporous morphologies and scrupulous nanoarchitectures, the Co3O4 nanobelts show excellent electrochemical performances such as high storage capacity and superior rate capability. The specific capacity of Co3O4 nanobelts could remains over 614 mA h g-1 at a current density of 1 A g-1 after 60 cycles. Even at a high current density of 3 A g-1, these Co 3O4 nanobelts still could deliver a remarkable discharge capacity of 605 mA h g-1 with good cycling stability. © 2012 American Chemical Society.