Piezoelectric properties of new ternary Bi 1/2 (Na, Li) 1/2 TiO 3 –(Bi 1/2 K 1/2 )TiO 3 –Ba 0.85 Ca 0.15 Ti 0.90 Zr 0.10 O 3 ceramics

Jiagang Wu,Sha Qiao,Jianguo Zhu,Dingquan Xiao

DOI: https://doi.org/10.1007/s00339-012-7297-4

2012-01-01

Abstract:0.852[Bi 1/2 (Na 1− x Li x ) 1/2 ]TiO 3 –0.110(Bi 1/2 K 1/2 )TiO 3 –0.038Ba 0.85 Ca 0.15 Ti 0.90 Zr 0.10 O 3 (BNLT–BKT–BCTZ- x ) new ternary piezoelectric ceramics were fabricated by the conventional solid-state method, and their piezoelectric properties as a function of the Li content were mainly investigated. A stable solid solution with a single perovskite structure has been formed, and the depolarization temperature ( T d ) of these ceramics was identified by using the temperature dependence of the dielectric loss. The T d value of these ceramics gradually decreases, while the T m value increases with increasing the Li content. The dielectric constant increases and the dielectric loss decreases with increasing the Li content, and an enhanced piezoelectric behavior of d 33 ∼223 pC/N and k p ∼35.2 % has been demonstrated in these ceramics with x =0.06.