Abstract:A novel micro/nanoscale rough structured superhydrophilic hybrid-coated mesh that shows underwater superoleophobic behavior is fabricated by spray casting or dipping nanoparticle–polymer suspensions on stainless steel mesh substrates. Water droplets can spread over the mesh completely; meanwhile, oil droplets can roll off the mesh at low tilt angles without any penetration. Besides overcoming the oil-fouling problem of many superhydrophilic coatings, this superhydrophilic and underwater superoleophobic mesh can be used to separate oil and water. The simple method used here to prepare the organic–inorganic hybrid coatings successfully produced controllable micro-nano binary roughness and also achieved a rough topography of micro-nano binary structure by controlling the content of inorganic particles. The mechanism of oil–water separation by the superhydrophilic and superoleophobic membrane is rationalized by considering capillary mechanics. Tetraethyl orathosilicate (TEOS) as a base was used to prepare the nano-SiO2 solution as a nano-dopant through a sol-gel process, while polyvinyl alcohol (PVA) was used as the film binder and glutaraldehyde as the cross-linking agent; the mixture was dip-coated on the surface of 300-mesh stainless steel mesh to form superhydrophilic and underwater superoleophobic film. Properties of nano-SiO2 represented by infrared spectroscopy and surface topography of the film observed under scanning electron microscope (SEM) indicated that the film surface had a coarse micro–nano binary structure; the effect of nano-SiO2 doping amount on the film’s surface topography and the effect of such surface topography on hydrophilicity of the film were studied; contact angle of water on such surface was tested as 0° by the surface contact angle tester and spread quickly; the underwater contact angle to oil was 158°, showing superhydrophilic and underwater superoleophobic properties. The effect of the dosing amount of cross-linking agent to the waterproof swelling property and the permeate flux of the film were studied; the oil–water separation effect of the film to oil–water suspension and oil–water emulsion was studied too, and in both cases the separation efficiency reached 99%, which finally reduced the oil content to be lower than 50 mg/L. The effect of filtration times to permeate flux was studied, and it was found that the more hydrophilic the film was, the stronger the stain resistance would be, and the permeate flux would gradually decrease along with the increase of filtration times.

Photo-Induced Water-Oil Separation Based On Switchable Superhydrophobicity-Superhydrophilicity And Underwater Superoleophobicity Of The Aligned Zno Nanorod Array-Coated Mesh Films

Ph-Controllable On-Demand Oil/Water Separation On The Switchable Superhydrophobic/Superhydrophilic And Underwater Low-Adhesive Superoleophobic Copper Mesh Film

Micro/Nanoscale Hierarchical Structured Zno Mesh Film For Separation Of Water And Oil

On-demand oil/water separation enabled by magnetic super-oleophobic/super-hydrophilic surfaces with solvent-responsive wettability transition

Phototunable Underwater Oil Adhesion of Micro/Nanoscale Hierarchical‐Structured ZnO Mesh Films with Switchable Contact Mode

Ni-Al Layered Double Hydroxides (ldhs) Coated Superhydrophobic Mesh with Flower-Like Hierarchical Structure for Oil/water Separation

Highly-efficient Separation of Oil and Water Enabled by a Silica Nanoparticle Coating with Ph-Triggered Tunable Surface Wettability

Ph-Induced Reversible Wetting Transition Between the Underwater Superoleophilicity and Superoleophobicity.

A durable Ni3S2 coated mesh with reversible transition between superhydrophobicity and underwater superoleophobicity for efficient oil-water separation

Multifunctional Switchable Nanocoated Membranes for Efficient Integrated Purification of Oil/Water Emulsions

Hygro-responsive, Photo-decomposed Superoleophobic/Superhydrophilic Coating for On-Demand Oil-Water Separation

A Ph-Responsive Superwetting Nanostructured Copper Mesh Film for Separating Both Water-in-oil and Oil-in-water Emulsions

Facile fabrication of durable mesh with reversible photo-responsive wettability for smart oil/water separation

pH-Responsive Multifunctional Materials with Switchable Superamphiphobicity and Superoleophobicity-Superhydrophilicity for Controllable Oil/Water Separation

Environmentally Benign Development of Superhydrophilic and Underwater Superoleophobic Mesh for Effective Oil/water Separation

pH‐Responsive Superwettability Surface: The Study of Oil Dewetting Ability from Air to Water on a Rough Surface and Selective Oil‐Water Separation

Robust Photopolymerized Superoleophobic/Superhydrophilic Mesh for Oil-Water Separation

Photocontrollable water permeation on the micro/nanoscale hierarchical structured ZnO mesh films.

Micro/Nanoscale Structured Superhydrophilic and Underwater Superoleophobic Hybrid-Coated Mesh for High-Efficiency Oil/Water Separation

A self-cleaning TiO2 coated mesh with robust underwater superoleophobicity for oil/water separation in a complex environment

Highly stable superamphiphobic material with ethanol-triggered switchable wettability for high-efficiency on-demand oil–water separation