Effects of Aluminum and Molybdenum Content on the Microstructure and Properties of Multi-Component Γ′-Strengthened Cobalt-Base Superalloys
Yi Zhang,Huadong Fu,Xiaozhou Zhou,Yuheng Zhang,Jianxin Xie
DOI: https://doi.org/10.1016/j.msea.2018.09.058
2018-01-01
Abstract:Five novel Co-30N1-(6 + x)Al-(3-y)W-yMo-1Ta-3.5Ti-12Cr-0.1Hf-0.025 C (x = 0, y = 0, 1, and x = 2, y = 0, 1, 2 at%) multi-component polycrystalline gamma'-strengthened Co-base superalloys are designed to investigate the effects of Al and Mo content on the microstructure and properties in this study. Based on the 6Al3W alloy, the addition of 2 at% Al has the effects of increasing the gamma' solvus temperature, reducing the density, increasing the gamma' volume fraction and coarsening rate, reducing the Vickers hardness but increasing the yield strength at 750 degrees C. The replacement of 1 at% W by 1 at% Mo remarkably reduced the density with a negligible effect on the gamma' coarsening rate; Meanwhile, this slightly reduced the gamma' solvus temperature and volume fraction causing a slight decrease of Vickers hardness and yield strength at 750 degrees C. The experimental alloys all show relatively low density, large processing window, good microstructure stability at 750 degrees C and mechanical properties, especially for 6Al2W1Mo alloy which has density of 8.69 g cm(-3), processing window of 247 degrees C, room-temperature Vickers hardness of 5.1 GPa, stable microstructure without detrimental phase after a heat treatment of 900 degrees C @8 h + 750 degrees C @1000 h. These results may provide guidance for the development of the novel wrought Co-base superalloys with high performance and low density.