Mechanical Properties and in Vitro Degradation of Electrospun Bio-Nanocomposite Mats from PLA and Cellulose Nanocrystals

Qingfeng Shi,Chengjun Zhou,Yiying Yue,Weihong Guo,Yiqiang Wu,Qinglin Wu

DOI: https://doi.org/10.1016/j.carbpol.2012.05.042

IF: 10.723

2012-01-01

Carbohydrate Polymers

Abstract:Fibrous bio-nanocomposite mats consisting of cellulose nanocrystals (CNCs) and poly(lactic acid) (PIA) were electrospun from a solvent mixture consisting of N,N'-dimethylformamide and chloroform at room temperature. Morphological, mechanical and thermal properties, as well as in vitro degradation of nanocomposite mats were characterized as a function of material composition. Average diameter of the electrospun fibers decreased with increased CNC-loading level. Thermal stability, and tensile strength and modulus of nanocomposite mats were effectively improved by the addition of CNCs up to the 5 wt% level. The reinforcement of CNCs on electrospun mats was illustrated by the observation of SEM-based morphologies on the tensile fracturing process of nanocomposite mats. At the CNC content of 5 wt%, the maximum tensile stress and Young's modulus of the nanocomposite mats increased by 5 and 22 folds than those of neat PEA mats, respectively. Moreover, compared with neat PEA mats, the nanocomposite mats, especially at high CNC-loading levels, degraded more rapidly in phosphate-buffered saline solution. (C) 2012 Elsevier Ltd. All rights reserved.