Influence of Incremental Rate of Anodising Current on Roughness and Electrochemical Corrosion of Oxide Film on Titanium Alloy Ti–10V–2Fe–3Al

J. H. Liu,G. L. Wu,M. Yu,L. Wu,Y. Zhang,S. M. Li
DOI: https://doi.org/10.1179/1743294411y.0000000091
IF: 2.451
2012-01-01
Surface Engineering
Abstract:In this study, the influence of incremental rate of anodising current VIR on the crystal structure, surface roughness and corrosion resistance of anodic oxide films on Ti–10V–2Fe–3Al was studied using Raman spectroscopy, atomic force microscopy (AFM), electrochemical impedance spectroscopy (EIS) and potentiodynamic polarisation. The results showed that the surface roughness, crystal structure and electrochemical corrosion behaviour of anodic oxide films were remarkably affected by different VIR with regard to the change in the rate of anodising voltage. In addition, results of EIS and potentiodynamic polarisation revealed that the film that formed at VIR of 0··50 A min−1 had the highest corrosion resistance. Quantitative AFM characterisation showed good correlation between surface roughness and EIS results. Furthermore, results of Raman spectroscopy showed that the relative intensity of anatase and rutile had a tendency to increase with a decrease in VIR before reaching 0··50 A min−1.
What problem does this paper attempt to address?