Effects of Dibenzocrown Ether and Diphenoxyethylene Diether Structural Units on the Properties of Degradable Polyhexahydrotriazine Thermosetting Resins
Yu Zheng,Shi-jing Yan,Yan Zhang,Wei-ging Rong,Ying-ying Han,Chun Lu,Jian Wu
DOI: https://doi.org/10.11777/j.issn1000-3304.2022.22050
2022-01-01
Acta Polymerica Sinica
Abstract:Polyhexahydrotriazine (PHTs) films were prepared by polycondensation between the two aromatic diamine monomers and paraformaldehyde and then the thermal curing process. Those two aromatic diamine monomers were 4,4 '-diaminodibenzocrown ether (DACr) and 2,2-bis(P-aminophenoxy) ether (BAPE), which contained both flexible ether and rigid benzene ring structures. Through structural characterization and a variety of performance tests, including thermal performance analysis, tensile testing, contact angle, chemical resistance performance testing, and degradation performance testing, the effect of structural units of DACr and BAPE on the crosslinking structures formation and properties of polymer were investigated. The results show that the rigidity of the structural unit was related to the completeness of the cross-linked structure of the hexahydrotriazine (HT) ring and jointly determined the performance of the PHT film material. The PHT containing the flexible acyclic BAPE structural unit tended to form perfect HT rings, and behaved the high thermal stability (5% thermogravimetric loss temperature is 296.8 degrees C), hydrophilicity and relatively low degree of acid hydrolysis. The PHT film containing the more rigid DACr structural unit had the higher mechanical strength (tensile strength 53.6 MPa), hydrophobicity, resistance to organic reagents and the degree of acid hydrolysis, it was complete degaration in glacial acetic acid solution and recyling the raw monomer of DACr with high yield of more than 83%. Due to the influence of both the structural integrity of HT and the rigidity of the structural unit, the two PHT materials showed the similar glass transition temperatures (T(g)s were 117.8 and 117.9., respectively). This study provides theoretical basis and experience for the structural design and performance regulation of PHT materials. Meantime, the obtained PHT materials meet the degradation requirements and have the potential application value.