Synthesis of Ultraviolet Curable Hyperbranched Polyurethane Acrylate and Properties of Its Cured Films
肖文清,涂伟萍
DOI: https://doi.org/10.3321/j.issn:1003-9015.2009.02.011
2009-01-01
Abstract:Hyperbranched aliphatic polyester terminated with 16 hydroxyl groups was synthesized by one step polymerization process with 2,2-Bis(methylol)propionic acid as branched monomer and neopentyl glycol as core molecule.Through further reacting with isocyanate groups of self-prepared toluene diisocyanate hydroxypropyl acrylate monomer,the obtained polyester was transformed into a novel UV-curable hyperbranched polyurethane acrylate(HBPUA).The IR was used to analyze the chemical structures of hyperbranched polyester,HBPUA and its UV-cured film,respectively.The effects of functional monomer and its amount on physical properties and thermal stability of the HBPUA UV-cured films were studied by means of mechanical propertied test,DSC and TG analyses.The results show that,with the increase of the amount of active monomer,impact strength of the films increases and its hardness decreases,while the hardness of the film would increase with the increase of functional degree of active monomer.The TG analyses demonstrate that the films have two thermolysis temperatures of 200℃and about 375℃,and the DSC results show that the films have two glass transition temperature too(Tg.s,Tg,h),with the increase of functional degree of active monomer,the Tg.s of the films decreases,while its Tg.h increases;this phenomenon is favorable for phase separation. However increasing the amount of used diluents will hinder the phase separation.Furthermore,the curing behaviors of HBPUA were tracked with IR and gel analysis,and the results show that the ultimate double bond conversion excesses 90%.