Abstract:We demonstrate a simple and effective approach to control the diameter of ultrathin ZnO nanowires with high aspect ratios and high densities over large areas. Diblock copolymer-based nanoparticle arrays exhibiting a high degree of hexagonal order and offering easy control of particle size (typically 1-10 nm) and interparticle spacing (25-150 nm) are utilized as nanocatalysts for the subsequent growth of semiconductor nanowires. The as-grown ZnO nanowires exhibit a single crystal hexagonal wurtzite structure and grow along the [0002] direction. Facetted catalyst particles were observed at the tip of the nanowires after synthesis, thus suggesting a catalyst-assisted vapor-solid-solid (VSS) rather than a vapor-liquid-solid (VLS) growth mechanism, the latter being frequently used in semiconductor nanowire production. Such a growth process allows us to easily prepare ultrathin ZnO nanowires with tunable diameters well below 10 nm by taking advantage of the inherent size control of the micellar method during deposition of the catalyst nanoparticles. Raman spectroscopy reveals a phonon confinement effect as the diameter of nanowires decreases. Photoluminescence spectra of these ultrathin nanowires indicate a blue shift of the free excitons and their phonon replicas by 37 meV induced by quantum confinement.

Synthesis of Vertically Aligned Ultra-Long ZnO Nanowires on Heterogeneous Substrates with Catalyst at the Root.

Carbon-Assisted Synthesis of Aligned Zno Nanowires

Synthesis of Vertical Arrays of Ultra Long ZnO Nanowires on Noncrystalline Substrates

Low-temperature, Catalyst-Free Vapor–solid Growth of Ultralong ZnO Nanowires

Alignment-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

Studies on the Synthesis and Growth Mechanism of Single Crystal ZnO Nanowires

On the formation of well-aligned ZnO nanowall networks by catalyst-free thermal evaporation method

Regrowth of template ZnO nanowires for the underlying catalyst-free growth mechanism

Catalyst-free Synthesis of Well-Aligned ZnO Nanowires on In0.2Ga0.8N, GaN, and Al0.25Ga0.75N Substrates.

Controlled Synthesis of Ultrathin ZnO Nanowires Using Micellar Gold Nanoparticles As Catalyst Templates.

Controllable Preparation of 1-D and Dendritic ZnO Nanowires and Their Large Area Field-Emission Properties

Controllable Growth of Laterally Aligned Zinc Oxide Nanorod Arrays on A Selected Surface of the Silicon Substrate by A Catalyst-Free Vapor Solid Process - A Technique for Growing Nanocircuits

Selective Growth of Vertical-aligned ZnO Nanorod Arrays on Si Substrate by Catalyst-free Thermal Evaporation

Growth of Arrayed ZnO Nanowires Using a Solution Method

Growth mechanism and diameter control of well-aligned small-diameter ZnO nanowire arrays synthesized by a catalyst-free thermal evaporation method.

Wafer-scale High-Throughput Ordered Growth of Vertically Aligned ZnO Nanowire Arrays.

Patterned growth of vertically aligned ZnO nanowire arrays on inorganic substrates at low temperature without catalyst.

Growth of Vertically Aligned ZnO Nanowire Arrays on ZnO Single Crystals

A Low-Temperature Aqueous Solution Route to Large-Scale Growth of Zno Nanowire Arrays

Conversion of ZnO nanorod arrays into ZnO/ZnS nanocable and ZnS nanotube arrays via an in situ chemistry strategy.

Low-temperature Growth and Raman Scattering Study of Vertically Aligned ZnO Nanowires on Si Substrate