Abstract:Nanocrystalline Ti1- x Crx O2 (0 ≤ x ≤ 0.20) samples were synthesised via acid-modified sol-gel process and characterised with various techniques, such as HRTEM, FESEM, Raman, XPS, DTA and VSM. The TEM image of TiO2 exhibits elongated nanoparticles with an average size of 10 nm. The HRTEM in combination with selected area electron diffraction (SAED) reveals the interplanar spacing and polycrystalline nature of the samples, respectively. FESEM micrographs divulge nonuniform morphologies and less aggregation of the particles in the doped sample. Raman spectra ensure the phase purity of the samples and a blue shift on Cr doping. X-ray photoelectron spectra (XPS) predict the chemical state of the elements and oxygen vacancies in the prepared samples. Room temperature magnetic measurements exhibit a significant variation in the magnetic parameters on Cr doping in TiO2 . The differential thermal analysis (DTA) shows the structural phase transition at ∼630°C. The photocatalytic performance is studied for the degradation of methylene blue (MB) dye under visible light irradiation. A higher photocatalytic efficiency is found for the 20% of Cr-doped TiO2 . These studies propose that the appropriate incorporation of Cr ions makes TiO2 very efficient for visible light-driven photocatalysts required for applications in wastewater treatment. LAY DESCRIPTION: In the present study, nanoparticles of TiO2 and Cr-doped TiO2 have been synthesised by a cost-effective acid-modified sol-gel process. The effect of Cr doping on the microstructure, thermal, magnetic and photocatalytic properties of TiO2 were explored in detail. The transmission electron microscopy (TEM) images exhibit the presence of elongated nanoparticles with an average size of 10 nm. Field emission scanning electron microscopy (FESEM) was used to study the surface morphology of the synthesised materials, which revealed nonuniform morphologies and less aggregation of the particles in the Cr-doped sample. Energy dispersive x-ray spectroscopy (EDS) confirms the elemental compositions with the appropriate stoichiometry of the elements. Raman spectra ensure the phase purity of the materials and also a blue shift with the incorporation of Cr ions in TiO2 . X-ray photoelectron spectra (XPS) predict the chemical state of the elements and oxygen vacancies in the prepared samples. The magnetic nature of all the synthesised samples was examined through the vibrating sample magnetometer (VSM) and revealed weak ferromagnetic behaviour of the samples. These results signify that the oxygen vacancies and defects play a crucial role in developing the ferromagnetic nature of oxide semiconductors. The differential thermal analysis (DTA) shows the structural phase transition at ∼630°C. The photocatalytic performance of the prepared samples was studied for the degradation of methylene blue (MB) dye under irradiation of visible light. A higher photocatalytic efficiency was found for the 20% of Cr-doped TiO2 . These studies propose that the appropriate incorporation of Cr ions makes TiO2 very efficient for visible light-driven photocatalysts required for applications in wastewater treatment.

Synthesis and Characterization of Natural Zeolite Supported Cr-doped TiO2 Photocatalysts

Influence Of Crystallization Of Nano Tio2 Prepared By Adsorption Phase Synthesis On Photodegradation Of Gaseous Toluene

Effect of Calcination Temperature on Crystal Structure and Photocatalytic Prop- Erty of TiO2/Diatomite Nanoparticles

Photodegradation of an Azo Dye Using Immobilized Nanoparticles of TiO2 Supported by Natural Porous Mineral.

Effect of Natural Zeolite Supports for Photoactive TiO2 During the Photodegradation Process

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Synthesis and Photocatalysis Properties of Sulfur Doped Nanocrystalline TiO2 Photocatalyst

Synthesis and characterization of ZnTiO3 with high photocatalytic activity

One-step synthesis of highly active Ti-containing Cr-modified MCM-48 mesoporous material and the photocatalytic performance for decomposition of H 2S under visible light

Preparation of Nanoparticle WO_3-doped TiO_2 and Research on Its Photocatalytic Activity

Preparation of AgI Sensitized Amorphous TiO2 As Novel High-Performance Photocatalyst for Environmental Applications

Design of TiO2 Nanocrystals with Enhanced Sunlight Photocatalytic Activity by Exploring Calcining Conditions

Preparation, characterization and photocatalytic properties of ZnTiO3 powders

Preparation, characterization and photocatalytic activity of silver-modified TiO2/zeolite catalysts

Physical properties and photocatalytic activity of Cr-doped TiO2 nanoparticles

Preparation and Characterization of Nanosized Anatase TiO2 Cuboids for Photocatalysis

Photocatalytic property of titanium silicate zeolite

Structural and Photocatalytic Properties of TiO2/Zeolite Synthesized using Sol-Gel Method

Preparation, Characterization and Photocatalytic Activity of Cr-Doped Rutile Tio2(110) Single Crystal Thin Films

Controllable Synthesis and Tunable Photocatalytic Properties of Ti3+-doped TiO2