Microstructural Characterization Of Fe-Mn-C Ternary Alloy Under Near-Rapid Solidification

Wenbin Xia,Rong Yang,Changjiang Song,Qijie Zhai

DOI: https://doi.org/10.1002/9781118371305.ch5

2012-01-01

Abstract:This paper focus on the influence of carbon content and cooling rate on the microstructure and phase formation of Fe-Mn-C alloys under near-rapid solidification. When manganese content is about 11wt.%, more epsilon-martensite can be obtained with cooling rate increasing when carbon content is 0.14wt.%, the formed phase changed from alpha phase to gamma phase when 0.74wt.% carbon is added to the samples, and when carbon content up to 2.1wt.%, carbide can be obtained in the sample. A host of stacking fault, which attributes to the strain-induced martensite, can be observed in the sample. The microhardness increased with cooling rate increasing, and under the same cooling rate, the microhardness of samples with 0.14wt.% carbon is highest.