Preparation and Photovoltaic Performances of CdSe Tetrapod Sensitized TiO2 Nanotube Arrays Solar Cells

Liang Chunjie,Leng Limin,He Jun,Pang Qi,Zhou Liya,Luo Jiwen

DOI: https://doi.org/10.3969/j.issn.0258-7076.2012.02.019

2012-01-01

Abstract:CdSe tetrapod nanocrystal and quantum dots (QDs) were combined with TiO 2 nanotube arrays, which were grown vertically on Ti substrate by using anodic oxidation method, to demonstrate a new type of quantum-dot-sensitized solar cells. The nanotube arrays could improve electron transport by avoiding the particle to particle hopping that occurred in the TiO 2 nanocrystalline membrane and the colloidal CdSe tetrapods were immobilized over the TiO 2 nanotube layers on account of tetrapod-shape structure. XRD, SEM and HR-TEM were used to characterize the nanotube and CdSe tetrapods, quantum dot. XRD results showed that samples were mixture phase with TiO 2 anatase and CdSe. SEM results showed that TiO 2 nanotubes were orderly arrays with diameter of about 120 nm and length of 13.8 μm. TEM showed that the CdSe quantum dots were tetrapod shape. The I-U curve showed that CdSe tetrapods could be used to sensitize the TiO 2 nanotube arrays making it highly responsive to the visible spectrum. Furthermore, for three-electrode measurement, a higher power conversion efficiency of 0.30% was obtained for CdSe tetrapod sensitized TiO 2 nanotube sample comparing with 0.13% for quantum dots sensitized TiO 2 nanotube under AM 1.5100 mW·cm -2 illumination.