Preparation of Carbon-Coated LiNi1/3Co1/3Mn1/3O2 Cathode for High-Rate Lithium Ion Batteries
Zheng Zhuo,Guo Xiao-Dong,Wu Zhen-Guo,Xiang Wei,Hua Wei-Bo,Zhong Ben-He,Yang Xiu-Shan
DOI: https://doi.org/10.11862/CJIC.2017.020
2017-01-01
Chinese journal of inorganic chemistry
Abstract:A series of carbon-coated LiNi1/3Co1/3Mn1/3O2 cathodes (w=1.0%, 2.0%, 3.0%) have been prepared by the carbonate co-precipitation, high temperature solid state method. Powder X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), electrochemical impedance spectroscopy (EIS) and galvanostatic charge-discharge tests were employed to analyze the crystal structure, micromorphology and electrochemical properties of the as-prepared materials. The results indicate that carbon was successfully coated on the particle surface, and the carbon-coated LiNi1/3Co1/3Mn1/3O2 cathodes have well-ordered alpha-NaFeO2 structure (Space group: R (3) over barm). The average primary particle sizes were gradually increased (from 177 to 209 nm) with the increased carbon coating. The amorphous carbon layer on the surface could enhance the electronic conductivity and decrease the side reactions between electrolyte and electrodes, thus improving the electrochemical performance. The 2.0% carbon-coated sample has the best high rate and long-term cycling stability. After 100 cycles at 1C between 2.7 and 4.3 V, the material retained 93% of its initial capacity. At 0.1C, 0.2C, 0.5C, 1C, 3C, 5C, 10C and 20C, the specific capacities of the material were 155, 148, 145, 138, 127, 116, 104 and 96 mAh.g(-1), respectively. This sample exhibits an excellent ultra-high rate performance with a high discharge capacity of 62 mAh.g(-1) (the pristine LiNi1/3Co1/3Mn1/3O2 barely delivers 30 mAh.g(-1)) even at the ultra-high rate 50C (9 A.g(-1)).