Hg 0 removal performance at low temperature by mesoporous MOF-derived Cr 2 O 3 nanoparticle with enriched metal sites and oxygen vacancy: Mechanism study on the role of oxygen species
Xifeng Zhu,Yuan Liu,Yi Xiao,Longchun Zhong,Tao Wang,Yuguo Wang,Wei-Ping Pan
DOI: https://doi.org/10.1016/j.cej.2023.143402
IF: 15.1
2023-05-18
Chemical Engineering Journal
Abstract:The oxidation adsorption of Hg 0 by metal oxide is an effective method to remove Hg 0 . A novel high-performance catalyst Cr 2 O 3 -MOF was prepared by direct calcination of MIL-101 (Cr) to improve the mercury adsorption capacity of MOFs at lower temperature ranges, overcome the weak resistance to different flue gas components and increase the recycling capacity. Cr 2 O 3 -MOF retains the skeleton structure of MOF with small particle sizes and scattered active sites. The oxygen vacancy (O V ) formed after calcination can be filled by free oxygen to adjust the catalytic performance of the surface. Thus, Cr 2 O 3 -MOF has a mercury removal capacity to be reached at 100% in a wide temperature range (30–200 °C), especially has the ability of mercury adsorption at room temperature that many MOF adsorbents do not have. After continuous adsorption at 30 °C for 50 h, the mercury removal efficiency was maintained at 90.3%, and it could be recycled. Cr 2 O 3 -MOF also has excellent resistance to flue gas components such as SO 2 , NH 3 , NO, and H 2 O. Based on different characterization methods and density functional theory (DFT), the transition state theory explains that adsorbed oxygen (O Ads ) filled in O V has higher mercury capture activity than that of natural lattice oxygen (O Lat ) in the adsorbent. More importantly, compared with noble metal supported monatomic catalysts, Cr 2 O 3 -MOF has a lower cost with higher mercury removal efficiency, it has more industrial application prospects.
engineering, chemical, environmental