Improving the Microstructure and Mechanical Properties of Laser-Welded Al–Si-Coated 22MnB5/Galvanized Steel Joints Added by Nickel
Youping Zhang,Youqiong Qin,Feng Zhao,Min Liang
DOI: https://doi.org/10.3390/met13091600
IF: 2.695
2023-09-16
Metals
Abstract:To weaken the harm of Al–Si coating and increase the strength of welded joints, variable thicknesses of Ni foil (Ni, an austenitic formation element) were added to the lap laser welding Al–Si-coated 22MnB5 hot stamping steel/galvanized steel joints. The joints' weld appearance, microstructure, and mechanical properties were explored. The weld altered from an X shape to a Y shape with an increased thickness of Ni foil. During welding, Al–Si coating was melted and diluted into the welding pool, forming δ-ferrite (a rich-Al phase with low toughness and strength) in the fusion zone (FZ) and fusion boundary (FB). This phase deteriorated the strength of the joints. After adding Ni, the amount and size of the δ-ferrite phase decreased. With a significant thickness of Ni foil, δ-ferrite disappeared. However, a new phase (fresh martensite (FM), which formed at low temperature and contained rich Ni) probably formed, except PM (previous martensite (PM), which formed at high temperature and contained little Ni or no Ni). The heat-affected zone (HAZ) on the side of 22MnB5 comprised a coarse martensite zone, refined martensite zone, martensite + ferrite zone, and tempered martensite zone from the FZ to the basic material. HAZ on the side of galvanized steel mainly contained ferrite and pearlite. After adding the Ni foil, the strength of the joint was greater than that without Ni. The maximum strength of the joint can be up to 679 MPa because of the disappearance of δ-ferrite. Meanwhile, the toughness of the joint increased. The fracture mode was from three mixed fractures (cleavage, quasi-cleavage, and dimple) to one fracture (dimple).
materials science, multidisciplinary,metallurgy & metallurgical engineering