Influence of Secondary Phases on Dynamic Recrystallization Mechanisms in Extruded Mg-Zn-Y Magnesium Alloy

HE Wei-wei,ZHANG Kun,HUANG Min,DAI Sheng-long

DOI: https://doi.org/10.3969/j.issn.1005-5053.2012.5.002

2012-01-01

Abstract:The combination of low density and moderate strength makes wrought magnesium alloys well suited for the application where weight is of critical importance.In recent years,magnesium alloys containing rare earth Y element have been developed and extensively investigated.Mg-Zn-Y alloys have high specific strength and good creep resistance due to the presence of quasicrystals.The aim of the present study is to investigate DRX behavior and mechanism in extruded Mg-Zn-Y magnesium alloys with different secondary phases(I-phase and W-phase) using Gleeble-3800 thermo mechanical simulator at the temperature range of 250～400℃(in step of 50℃) and in the strain range of 0.001～10s-1.The microstructures of the alloy in the different stages of processing were examined by optical microscopy(OM) and transmission electronic microscopy(TEM).The conclusions have been drawn from investigation are:at high temperature of 400℃ and strain rate of 1s-1,when true strain was low(0.1 or 0.3),DRX mechanism of alloy with I-phase is normal as the ordinary DRX.When the true strain was high(0.5),the DRX mechanism of alloy with W-phase is CDRX.At temperature of 300℃ and strain rate of 1s-1,when the true strain was low,DRX mechanism of alloy with W-phase is CDRX,and when true strain was higher,and its DRX mechanism was the RDRX.Because of the DRX mechanisms of alloys with different secondary phases are different,the effect of temperature on microstructure of the alloy after deformation were also different.For alloy with I-phase,grain size of DRX was decreased with deformation temperature increased but for alloy with W-phase,DRX grain grows abnormally.The microstructure of alloy with W-phase after deformation could be refined efficiently by increasing the strain.