Structural, Magnetic, and Ferroelectric Phase Transitions and Energy Storage Efficiency in Ba1-xLaxTi1-xFexO3 Ceramics
T. P. Hoang,L. V. Truong-Son,Lien Phan,N. T. Nghiem,N. Truong-Tho,N. H. Tiep,S. H. Jabarov,D. P. T. Tien,T. A. Tran,N. T. Dang,D. D. Bich,D. T. Khan
DOI: https://doi.org/10.1007/s11664-024-11593-w
IF: 2.1
2024-11-20
Journal of Electronic Materials
Abstract:The co-substitution effect of La and Fe ions on structural characterization, ferroelectric and magnetic properties, and energy storage efficiency of multiferroics Ba 1- x La x Ti 1- x Fe x O 3 (0 ≤ x ≤ 0.20) was systematically studied utilizing a combination of x-ray diffraction, scanning electron microscopy, Raman spectroscopy, x-ray photoelectron spectroscopy (XPS), ferroelectric, and magnetic measurements. The results show a structural transformation from the P 4 mm tetragonal phase to the Pm -3 m cubic one at x = 0.04, with no hexagonal phase across the entire large doping range, which differs from the results previously reported for BaTiO 3 systems doped solely with Fe. The XPS results show single valence states of Ba, La, and Ti ions, alongside a mixed valence state of Fe in the investigated samples. Magnetic measurements indicate that the pristine sample ( x = 0) exhibits weak ferromagnetic (FM) phases within a diamagnetic (DM) matrix. At x < 0.10, the FM and DM phases are suppressed while the paramagnetic phase becomes dominant, indicating no interaction between Fe ions and a reduction in lattice intrinsic defects such as O and Ti vacancies. For 0.10 ≤ x ≤ 0.15, Fe ions start to couple with each other, enhancing the ferromagnetism. However, as x = 0.20, the saturation magnetization is significantly reduced, indicating competition between FM and antiferromagnetic interactions between Fe ions. Ferroelectric measurements demonstrate the ferroelectric nature of the lightly doped samples ( x ≤ 0.10) and the lossy improper ferroelectric nature of the samples with 0.15 ≤ x ≤ 0.20. The lossy improper ferroelectricity is related to electron hopping between the Fe 3+ –Fe 4+ interaction pathways. The coercive electric field, remnant polarization, and maximum polarization decrease with the increase of the porosity in the samples. Furthermore, Ba 1- x La x Ti 1- x Fe x O 3 exhibits high energy storage efficiencies of up to ~ 77%. These findings demonstrate an effective way to make efficient energy storage materials through optimizing doping level and morphological properties in BaTiO 3 and other ferroelectrics.
engineering, electrical & electronic,materials science, multidisciplinary,physics, applied