Abstract:In this work, the effect of graphene and nitrogen doping on the performance of dye-sensitized solar cells of pure TiO2 was studied. Pure and N-doped TiO2 nanoparticles were synthesized using a hydrothermal method, while graphene was prepared through the reduction of graphene oxide. The materials were characterized using x-ray diffraction (XRD), x-ray photoelectron spectroscopy (XPS), Fourier-transform infrared spectroscopy (FT-IR), Raman, Brunauer–Emmett–Teller surface area analysis (BET) and ultraviolet-visible (UV-Vis) diffusion reflectance spectroscopy. Nitrogen dopant concentration varied from 0 at.% to 1.57 at.%. The results confirmed that all N-doped samples exhibited pure anatase phase with an average diameter in the range of 7–12 nm. The pore volume and BET surface area increased with the amount of nitrogen in TiO2. XPS investigation displayed an N1s peak around 397 eV, which suggested N-Ti-O structure in the TiO2 matrix. Moreover, optical measurements showed that the optical absorption edge of N-doped TiO2 exhibited a significant shift from ultraviolet to visible light region in comparison with pure TiO2. Dye-sensitized solar cells (DSSCs) were fabricated using N719 dye and various TiO2 based photoanodes. The photoanode of N-doped TiO2 modified with graphene showed the highest energy-conversion efficiency of 6.3%, while the efficiencies of pure and N-doped TiO2 cells are 0.41% and 1.21%, respectively. The improvement in conversion efficiency of graphene-based DSSC was attributed to the formed electron bridges between TiO2 and fluorine-doped tin oxide (FTO), which led to a reduction in the recombination rate of electron-hole pairs and an increase in the rate of electron transport.

Nitrogen-Doped Graphene As Transparent Counter Electrode for Efficient Dye-Sensitized Solar Cells

Facile Synthesis of Nitrogen-Doped Reduced Graphene Oxide As an Efficient Counter Electrode for Dye-Sensitized Solar Cells

Graphene/polyaniline Nanocomposite As Counter Electrode of Dye-Sensitized Solar Cells

Nitrogen-doped graphene for dye-sensitized solar cells and the role of nitrogen states in triiodide reduction

Enhanced Electrocatalytic Performance of a Porous G-C3 N4 /graphene Composite As a Counter Electrode for Dye-Sensitized Solar Cells.

Edge-nitrogenated Graphene Nanoplatelets As High-Efficiency Counter Electrodes for Dye-Sensitized Solar Cells

Graphitic Carbon Nitride/multiwalled Carbon Nanotubes Composite As Pt-free Counter Electrode for High-Efficiency Dye-Sensitized Solar Cells

Back Cover: Nitrogen‐Doped Graphene Foams as Metal‐Free Counter Electrodes in High‐Performance Dye‐Sensitized Solar Cells (Angew. Chem. Int. Ed. 48/2012)

Synthesis of an Efficient Counter Electrode Material for Dye-Sensitized Solar Cells by Pyrolysis of Melamine and Graphene Oxide

Nitrogen-Doped Porous Carbon Prepared by A Facile Soft-Templating Process As Low-Cost Counter Electrode for High-Performance Dye-Sensitized Solar Cells

Dye-Sensitized Solar Cells Based on an N-Doped TiO2 and TiO2-Graphene Composite Electrode

N-doped graphene nanoribbons as efficient metal-free counter electrodes for disulfide/thiolate redox mediated DSSCs.

Synthesis of nitrogen-doped reduced graphene oxide as counter electrode material for dye-sensitized solar cells

CoSe2@N-Doped Graphene Nanocomposite High-Efficiency Counter Electrode for Dye-Sensitized Solar Cells

The Production of Polyaniline/graphene Hybrids for Use As a Counter Electrode in Dye-Sensitized Solar Cells

Interconnected Nitrogen and Sulfur Co-Doped Graphene-Like Porous Carbon Nanosheets with High Electrocatalytic Activity As Counter Electrodes for Dye-Sensitized and Quantum Dot-Sensitized Solar Cells

Nitrogen-doped carbon nanotube-based bilayer thin film as transparent counter electrode for dye-sensitized solar cells (DSSCs).

Low-cost Counter Electrodes Based on Nitrogen-Doped Porous Carbon Nanorods for Dye-Sensitized Solar Cells

Improved Performances of Graphite Counter Electrode for Dye-Sensitized Solar Cells by Incorporating Graphene Nanosheets

Enhanced Electrocatalytic Performance Of Graphene Via Incorporation Of Sio2 Nanoparticles For Dye-Sensitized Solar Cells

Low-Cost and Efficient Nickel Nitroprusside/Graphene Nanohybrid Electrocatalysts as Counter Electrodes for Dye-Sensitized Solar Cells