Abstract:The structure, phase composition, hardness, and tribological properties of composite gas-thermal 50% Cu–50% (Al–Si) coatings under various friction conditions were studied. It has been shown that during the process of high-speed metallization, active interaction of molten aluminum and copper particles occurs, leading to the formation of solid solutions and intermetallic compounds in sprayed coatings. In particular, in 50% Cu–50% (Al–Si) coatings, in addition to the matrix phases of Cu and Al, intermetallic compounds Cu 9 Al 4 , CuAl 2 , and Cu 3 Al are recorded. The hardness and microhardness of the composite are 180 HV 1 and 180–190 HV 0.025, respectively. It has been established that a composite coating of 50% Cu–50% (Al–Si) has higher wear resistance under various friction conditions than the widely used coating of CuSn11P-C antifriction bronze, obtained by centrifugal induction surfacing. In particular, in the environment of I-20A lubricant, the wear resistance of the composite coating exceeds the wear resistance of bronze by ≈1.2 times, in the environment of Litol-24 plastic lubricant, by ≈1.4 times, and with dry friction up to ≈2.8 times. It has been shown that during boundary friction, dislocations accumulate in aluminum particles of the composite, while in copper particles at elevated test pressures, a predominant formation of a subgrain structure occurs. Based on the studies conducted, it was concluded that the increased wear resistance of the composite is due to the presence of solid intermetallic compounds in it, solid solution strengthening, the presence of silicon in aluminum interlayers, as well as dislocation strengthening of aluminum interlayers and the formation of a subgrain structure in copper interlayers.

Formation of Laminar Structure under Unlubricated Friction of Cu–SiO2 Composite

Wear Behaviour and Microstructural Changes of SiCw-Al Composite under Unlubricated Sliding Friction

Tribological Behavior and Wear Mechanism of Cu-SiO2 Sintered Composite under Different Sliding Speeds

Formation of Nano-Laminated Structures in a Dry Sliding Wear-Induced Layer under Different Wear Mechanisms of 20crni2mo Steel

Formation of a Self-Lubricating Layer by Oxidation and Solid-State Amorphization of Nano-Lamellar Microstructures During Dry Sliding Wear Tests

Frictional Shear-Induced Nanolamellar Oxidation and Transformation to Oxide Nanoparticles During Pearlitic Steel Sliding

Friction anisotropy and associated surface deformation mechanisms in heterogeneous copper/bronze laminates

Formation and Evolution of Tribo-Layer on Al2O3 and Al2O3-Based Ceramics in Sliding Against Si3N4 under Dry Sliding

A Study of the Frictional Layer of Tial-12ag-5tib(2) Composite During Dry Sliding Wear

Formation of Friction Layers in Graphene-Reinforced TiAl Matrix Self-Lubricating Composites

Synergistic Effect of Cementite Amorphization and Oxidation on Forming a Nanocomposite Self-Lubricating Surface During Sliding

Effect of Sliding Condition and Wear Surface State on the Tribological Behaviour of SiCp/Cu Composite

New Insights into the Microstructure of the Friction Surface Layer of C/C Composites

Operando formation of multiphase heterostructure for achieving macroscale superlubricity with ultra-long lifetime under high contact stress

Lowering the Coefficient of Martensite Steel by Forming a Self-Lubricating Layer in Dry Sliding Wear

Self-Lubricant Effect of Tri-Oxidizing Layer in Surface of Bulk Ti3SiC2 Materials

Comparison of the Tribological Behavior of Columnar-Grained Polycrystalline Copper with Vertical/Horizontal Orientation Sliding Against Aisi 1045 Steel

Influence of structure parameters on the tribological properties of MoB/Cu laminated composites

Microstructural Investigation on Antifriction Characteristics of Self-Lubricating Copper Hybrid Composite

Substructural Changes in the Surface Layers of Composite Gas-Thermal Cu–(Al–Si) Coatings during Friction under Various Conditions

Self-lubricant effect of tri-oxidizing layer in surface of bulk Ti 3SiC2 materials