Abstract:Nickel-titanium shape memory alloy is a novel material with outstanding properties suitable for biomedical applications such as implantation devices. Unfortunately, the high composition of nickel in this alloy can be harmful to the human body, if its exposure exceeds a threshold value. Therefore, an innovative electrical discharge coating technique was investigated and proposed in this study to develop minimal microdefect formation with high corrosion resistance through fractional factorial design of experiment. The results showed that discharge duration mostly dominated the material deposition, microcracks, and porosity fraction up to 72%, due to the impact of the intensity of discharge energy. There was also a pronounced effect of titanium powder concentration in the deionized water on the percentage of titanium and nickel elements and microcrack formation. The powder suspension enhanced the recast layer formation through the increment of layer density, which covered up the Ni-rich region and diminished the microcrack formation. An optimized substrate recorded the lowest corrosion current, , and highest corrosion voltage, , at 3.43 × μA/cm 2 and − 0.07 V respectively, thus exhibiting an outstanding corrosion resistance rate at only 8.57 μm/year in phosphate-buffered saline solution, due to the low nickel concentration, low microcracks, and low porosity fraction in the recast layer. Therefore, the results obtained within this styud presented an initial step towards assessing the feasibility of applying the electrodischarge process to biomaterials, including nickel-titanium shape memory alloy. Further exploration, involving both in-vitro and/ or in-vivo studies, is essential to thoroughly evaluate the performance of the coating obtained from the process.

In Vitro Corrosion Inhibition on Biomedical Shape Memory Alloy by Plasma-Polymerized Allylamine Film

Enhanced corrosion resistance and hemocompatibility of biomedical NiTi alloy by atmospheric-pressure plasma polymerized fluorine-rich coating

Multifunctional Plasma-Polymerized Film: Toward Better Anticorrosion Property, Enhanced Cellular Growth Ability, and Attenuated Inflammatory and Histological Responses.

In vitro corrosion behavior of nano-multilayered TiN/Ti coated NiTi alloy

Enhanced Bioactivity of Biomedical Niti Through Surface Plasma Polymerization

Mechanical Properties, Bioactivity and Corrosion Resistance of Oxygen and Sodium Plasma Treated Nickel Titanium Shape Memory Alloy

Corrosion Behaviors of Sputtered NiTiCu Shape Memory Films

Modifying NiTi shape memory alloys to reduce nickel ions release through ethylenediamine plasma polymerization for biomedical applications

Xps and Biocompatibility Studies of Titania Film on Anodized Niti Shape Memory Alloy

Electrochemical and surface characterization of a nickel–titanium alloy

Effects of Plasma Polymerization on the Performance of Biomedical Titanium

Bioactivity and Corrosion Resistance of NiTi after Calcium Plasma Immersion Ion Implantation

Electrochemical Stability of Orthopedic Porous NiTi Shape Memory Alloys Treated by Different Surface Modification Techniques

The Corrosion Resistance, Biocompatibility and Antibacterial Properties of the Silver-Doped Dicalcium Phosphate Dihydrate Coating on the Surface of the Additively Manufactured NiTi Alloy

Plasma Surface Modification of Nickel Titanium Shape Memory Alloys

In vitro and in vivo characterization of novel plasma treated nickel titanium shape memory alloy for orthopedic implantation

Microstructure, Nickel Suppression and Mechanical Characteristics of Electropolished and Photoelectrocatalytically Oxidized Biomedical Nickel Titanium Shape Memory Alloy

Enhanced Corrosion Resistance of Zr Coating on Biomedical Tini Alloy Prepared by Plasma Immersion Ion Implantation and Deposition

Investigation into microdefects and corrosion resistance of nickel-titanium shape memory alloy using electrical discharge coating process

New plasma surface-treated memory alloys: Towards a new generation of “smart” orthopaedic materials

Pulsed‐Plasma Polymeric Allylamine Thin Films