Abstract:The development of acid-resistant and efficient corrosion inhibitors is of great significance for metal protection in many industrial processes. In this work, eight cases of sandwich-type polyoxometalate (POM)-based inorganic-organic hybrids, namely, carboxyethyltin and transition metal (TM) cofunctionalized tungstoantimonates and tungstobismuthates, formulated as Na x K10-x [(SnR)2(TM(H2O)3)2(B-β-SbW9O33)2]·mH2O and Na y K10-y [(SnR)2(TM(H2O)3)2(B-β-BiW9O33)2]·nH2O (abbreviated as SbW9-TM-SnR and BiW9-TM-SnR; TM = Mn, Co, Ni, and Zn; m = 18, 24, 24, and 22; n = 30, 25, 20, and 21; SnR = Sn(CH2CH2COO)) are first used as green corrosion inhibitors for 20# carbon steel in 0.5-2.0 M HCl solutions. Weight loss and electrochemical experiments prove that the corrosion inhibition efficiency is all above 81% for these POM-based corrosion inhibitors at 150 mg L-1, and SbW9-Mn-SnR shows the highest efficiency of 96.9% at 150 mg L-1 after immersion in a 0.5 M HCl solution for 10 h. Scanning electron microscopy-energy-dispersive X-ray spectroscopy and X-ray photoelectron spectroscopy analyses show that these POM-based inhibitors form films on the carbon steel and the adsorption mechanism obeys the Langmuir adsorption model. The thermodynamic activation parameters were calculated, proving the occurrence of both chemical and physical adsorptions. The film-forming mechanism was also analyzed. This work provides guidance for synthesizing new lacunary POM-based materials to protect metals from corrosion in HCl pickling.

Corrosion inhibition of Vitamins B for hot dipped Zn coating steel in hydrochloric acid

Experimental and Theoretical Investigation of 1-Hexyl-3-methylimidazolium Iodide As a Corrosion Inhibitor for Mild Steel in HCl Environment

Nicotinic acid derivatives as corrosion inhibitors for mild steel in hydrochloric acid solutions: an experimental and computational chemistry study

Corrosion inhibition of mild steel in acidic environments: Mechanistic insights and protective effects of azo-cum inhibitor

Effect of Hexagonal Boron Nitride Nanoparticles Additions on Corrosion Resistance for Zinc Coatings of Weathering Steel in Rainwater

Corrosion Resistance of Mild Steel in Hydrochloric Acid Solutions by Clinopodium acinos as a Green Inhibitor

Stevioside–Zn2+ system as an eco-friendly corrosion inhibitor for C1020 carbon steel in hydrochloric acid solution

The Application of Zinc Oxide Nanoparticles as An Eco- Friendly Inhibitor for Steel in Acidic Solution

Enhanced Corrosion Resistance of Carbon Steel in Hydrochloric Acid Solution by Polyoxometalate-Estertin Derivatives

CORROSION INHIBITION EFFECT OF BISQUATERNARY AMMONIUM SALT OF ROSIN GROUP TO MILD STEEL IN HYDROCHLORIC ACID

Novel Triazolyl Bis-Amino Acid Derivatives Readily Synthesized Via Click Chemistry As Potential Corrosion Inhibitors for Mild Steel in Hcl

Corrosion Properties of Steel Sheet with Zinc-base Alloyed Coatings

Bio-based ionic liquid as a corrosion inhibitor for mild steel in 5% HCl solution: Experimental and theoretical investigation

Investigations on corrosion resistance of steel coated with chromium-free ZTM conversion coating

Inhibition Synergism Between Alkyl Imidazoline and Potassium Iodide on the Corrosion of Carbon Steel in Citric Acid Solution

Corrosion Resistance Improvement of Mild Steel

Prevention of Q235 Steel Corrosion using Waterborne Rust Inhibitor

Quinoxaline Derivatives as Newly Acid Corrosion Inhibitors for Mild Steel: Synthesis, Electrochemical, and Theoretical Investigations

Corrosion Inhibition of Carbon Steel in Chloride-Acetate Solution and Stratal Water by Nitrogen-Containing Compounds

Corrosion inhibition performance of protein derived carbon quantum dots as corrosion inhibitors on low carbon steel in sulfuric acid solution

An Eco-Friendly Quaternary Ammonium Salt as a Corrosion Inhibitor for Carbon Steel in 5 M HCl Solution: Theoretical and Experimental Investigation