Synthesis And Photoluminescence Properties Of Tb3+ Doped Zro2 Hollow Spheres
Min Zhang,Chunrong Shan,Yigao Chen,Dianguang Liu,Meng Zhu,Haoran Hong,Chengyu Yang,Yiguang Wang,Shengju Song,Lin Zhang,Linan An
DOI: https://doi.org/10.1166/jnn.2017.13058
2017-01-01
Journal of Nanoscience and Nanotechnology
Abstract:ZrO2:Tb3+ hollow spheres were successfully fabricated with the resin microspheres as the template. The sample characterizations were carried out by means of X-ray diffraction (XRD), scanning electron microscope (SEM) and photoluminescence (PL) spectra. XRD results revealed Tb3+ doped samples were pure t-ZrO2 phase after being calcined at 873 K. SEM results exhibited these Tb3+ doped ZrO2 was hollow spheres, the diameter and thickness of which were about 450 nm and 50 nm, respectively. The PL spectra indicate that the D-5(4) -> F-7(5) (545 nm) electric dipole transition is the most intensive when excited at 235 nm. It is shown that the 2.0 mol% of doping concentration of Tb3+ ions in t-ZrO2:Tb3+ is optimum. According to Dexter's theory, the critical distance between Tb3+ ions for energy transfer was determined to be 15 angstrom. It is found that the decay curves follow the single-exponential decay. The convenient synthetic procedure, excellent reproducibility, clean reactions, high yield, and fine quality of products in the work make the present route attractive and significant.