Cubic Ba 2 LaF 7 :Yb 3+ /ln(ln = Er 3+ ,ho 3+ ) Up-Conversion Submicron Particles Controllable Synthesis and Luminescence Properties
Zhang Xu,Shi Xueming,Hou Yuechun,Zhang Zhongyuan,Wang Xinyu,Yang Wenjing,Yang Weiling,Jilin Provincial Science and Technology Innovation Center of Optical Materials and Chemistry,Zhang Xuejian,Liu Huisheng,Huang KeKe
DOI: https://doi.org/10.1007/s10854-021-06945-9
2021-01-01
Journal of Materials Science Materials in Electronics
Abstract:In this paper, a co-doped cubic phase submicron particles Ba 2 LaF 7 :Yb 3+ /Ln 3+ (Ln = Er 3+ ,Ho 3+ ) up-conversion material were successfully synthesized by hydrothermal method. By adjusting PH, time, temperature, and the amount of sodium citrate during the preparation process, it was possible to analyze and obtain the phase structure, morphology, and up-conversion luminescence characteristics of the particles. Furthermore, the influence of doping concentration on the up-conversion luminescence characteristics was studied using X-ray diffractometer (XRD), scanning electron microscopy (SEM), fluorescence spectroscopy, and other characterization methods. The test results show that, under the conditions of pH = 9 and NaBF 4 as the fluorine source, Ba 2 LaF 7 :Yb 3+ /Ln 3+ (Ln = Er 3+ ,Ho 3+ ) spherical particles have an average size of 240 nm. Under the excitation of a 980 nm laser-diode (LD) laser, it was found that the material spectrum is mainly composed of strong green and weak red light. When Yb 3+ and Er 3+ doping concentrations are 18% and 2.5%, Yb 3+ and Ho 3+ doping concentrations are 18% and 3.5%, respectively, the up-conversion transmittance is the highest. Finally, the possible causes of the fluorescence decay curve of Ba 2 LaF 7 :Yb 3+ /Ln 3+ (Ln = Er 3+ ,Ho 3+ ) up-conversion materials were investigated.